Method for fabricating metal interconnections and wiring board having the metal interconnections
AssigneeSharp Kabushiki Kaisha
InventorsYoshihiro Izumi, Yoshimasa Chikama
Life of this patent
Estimating the term…
Abstract
A Ni film for a ground metal film is formed on an insulating substrate by direct current magnetron sputtering process, which prevents occurrence of minute protrusions on a surface of the ground metal film. Next, a Ni film is patterned into a specified interconnection form to obtain a patterned Ni film. Then, an anti-corrosive Au film having low resistance is formed on the patterned Ni film by electroless plating process. Further, an inexpensive Cu film having low resistance is formed on the Au film by electroplating process.
Claims18
A method for fabricating metal interconnections, comprising:
- a first step of forming a first metal film on an insulating substrate by a dry deposition technique;
- a second step of forming a second metal film selectively on the first metal film by displacement plating technique;
- and
- a third step of forming a third metal film selectively on the second metal film by electroplating technique or electroless plating technique using the second film as a catalyst.
A method for fabricating metal interconnections, comprising:
- a first step of forming a ground metal film on an insulating substrate by dry deposition technique;
- a second step of patterning the ground metal film into a specified pattern;
- a third step of forming an anti-corrosion metal film selectively on the patterned ground metal film by displacement plating technique;
- and
- a fourth step of forming a low-resistance metal film on the anti-corrosion metal film by electroplating technique or electroless plating technique using the anti-corrosion metal film as a catalyst.
A method for fabricating metal interconnections on a continuous, substantially flat surface of an insulating substrate, said method comprising the following steps:
- a first step comprising forming a first metal film having a thickness of between about 0.1 μm and about 0.2 μm on said continuous, substantially flat surface of said insulating substrate by a dry deposition technique;
- a second step comprising forming a second metal film having a thickness of between about 0.01 μm and about 0.1 μm selectively on the first metal film by a wet deposition technique;
- and
- a third step comprising forming a third metal film having a thickness between about 0.2 μm and about 0.4 μm selectively on the second metal film by a wet deposition technique;
- wherein the metal interconnections so fabricated are no more than about 0.5 μm thick.
A method for fabricating metal interconnections on a continuous, substantially flat surface of an insulating substrate, said method comprising the following steps:
- a first step comprising forming a ground metal film having a thickness of between about 0.1 μm and about 0.2 μm on said continuous, substantially flat surface of said insulating substrate by a dry deposition technique;
- a second step comprising patterning the ground metal film into a specified pattern;
- a third step comprising forming an anti-corrosion metal film having a thickness of between about 0.0 μm and about 0.1 μm selectively on the patterned ground metal film by an electroplating technique or an electroless plating technique;
- and
- a fourth step comprising forming a low-resistance metal film having a thickness between about 0.2 μm and about 0.4 μm selectively on the anti-corrosion metal film by a wet deposition technique;
- wherein the metal interconnections so fabricated are no more than about 0.5 μm thick.
Dependencies are inferred from the claim text.