A method of case-hardening a shaped object, comprising the steps of:

• etching a shaped object to produce a roughened surface on the shaped object;
• then immersing the shaped object in an aqueous solution of a metal salt of at least one of vanadium belonging to the VA group of the periodic table, chromium, molybdenum, and tungsten belonging to the VIA group of the periodic table, manganese belonging to the VIIA group of the periodic table, and nickel and cobalt belonging to the VIII group of the periodic table or at least one of the compounds thereof, and a solution of an organic salt and a metal of at least one of aluminum, yttrium, and lanthanum belonging to the III group of the periodic table, titanium, zirconium, silicon and hafnium belonging to the IV group of the periodic table, vanadium, tantalum, and niobium belonging to the VA group of the periodic table, and chromium, molybdenum and tungsten belonging to the VIA group of the periodic table or at least one of the compounds thereof;
• drying the shaped object;
• and
• thereafter, heating the shaped object to thereby produce a ceramic layer by nitriding, carburizing, carbonitriding or oxidizing on the surface of the shaped object and a metal-diffused layer in the shaped object formed inwardly of said ceramic layer.

A method of case-hardening a shaped object, comprising the steps of:

• cleaning tip of carbide or cermet on a shaped object with an alkaline solution;
• etching the tip with acid to produce a roughened surface on the tip;
• then, immersing the tip in an aqueous solution of a metal salt of at least one of chromium and tungsten belonging to the VIA group of the periodic table, manganese belonging to the VIIA group of the periodic table, and iron, nickel and cobalt belonging to the VIII group of the periodic table or at least one of the compounds thereof, or a solution of an organic salt and a metal of at least one of aluminum belonging to the III group of the periodic table, titanium and zirconium belonging to the IV group of the periodic table, vanadium belonging to the VA group of the periodic table, and chromium belonging to the VIA group of the periodic table or at least one of the compounds thereof;
• drying the shaped object;
• and
• thereafter, heating the shaped object to cause a diffusion reaction and thereby produce a ceramic layer by nitriding, carburizing, carbonitriding or oxidizing on the surface of the shaped object and a metal-diffused layer in the shaped object formed inwardly of said ceramic layer.

A method of case-hardening a shaped object, comprising the steps of:

• cleaning a tip of carbide or cermet on a shaped object with an alkaline solution;
• etching the tip with an acid to produce a roughened surface on the tip;
• then, immersing the tip in an aqueous solution of a metal salt of at least one of chromium and tungsten belonging to the VIA group of the periodic table, manganese belonging to the VIIA group of the periodic table, and iron, nickel and cobalt belonging to the VIII group of the periodic table or at least one of the compounds thereof, and a solution of an organic salt and a metal of at least one of aluminum belonging to the III group of the periodic table, titanium and zirconium belonging to the IV group of the periodic table, vanadium belonging to the VA group of the periodic table, and chromium belonging to the VIA group of the periodic table or at least one of the compounds thereof;
• drying the shaped object;
• and
• thereafter, heating the shaped object to cause a diffusion reaction and thereby produce a ceramic layer by nitriding, carburizing, carbonitriding or oxidizing on the surface of the shaped object and a metal-diffused layer in the shaped object formed inwardly of said ceramic layer.