Electroless plating bath composition and method for production thereof
AssigneeKosaku & Co., Ltd.
InventorsKazuhiro Fukuoka, Keiki Kiyohara, Tadayuki Konishi, Isao Miyatake, Masaji Hamamoto
Life of this patent
Estimating the term…
Abstract
An electroless plating bath composition is produced by mixing stannous oxide, at least one member selected from the group consisting of lead oxide and lead perchlorate, perchloric acid, and thiourea. The composition thus obtained is ideal for electroless plating of a substrate of copper, particularly a substrate provided with a resist film.
Claims2
An electroless plating bath composition for plating a substrate provided with a resist film, said bath produced by mixing sufficient amounts of:
- (a) stannous oxide,
- (b) at least one member selected from the group consisting of lead oxide and lead perchlorate,
- (c) perchloric acid and
- (d) thiorea
- such that the bath concentration of tin is from 6 to 22 g/l, the bath concentration of lead is from 8 to 30 g/l, the bath concentration of perchloric acid is from 19 to 58 g/l and the bath concentration of thiourea is from 20 to 70 g/l.
A method for the production of an electroless plating bath composition for plating a substrate provided with a resist film comprising the step of mixing sufficient amounts of:
- (a) stannous oxide,
- (b) at least one member selected from the group consisting of lead oxide and lead perchlorate,
- (c) perchloric acid and
- (d) thiourea
- such that the bath concentration of tin is from 6 to 22 g/l, the bath concentration of lead is form 8 to 30 g/l, the bath concentration of perchloric acid is from 19 to 58 g/l and the bath concentration of thiourea is from 20 to 70 g/l.
Dependencies are inferred from the claim text.