Hard surface coatings for metals in fluidized beds

Abstract

A process and apparatus for surface coating of workpieces in fluidized beds under atmospheric or slightly higher pressure is disclosed. The process comprises submerging the workpiece(s) in the fluidized bed, mixing a metal halide with an inert gas to form the fluidizing gas, feeding to the fluidized bed another gas which is capable of reacting with the metal halide in the fluidized bed and coating the workpiece(s). The workpiece(s) are maintained at a temperature in the range of from 1600.degree. F. to 2000.degree. F. until it is evenly coated. The apparatus comprises a saturator vessel for saturating the inert gas with the metal halide and a fluid bed reactor. There are several advantages that the present invention offers over the prior art, namely, the coating can be performed in a relatively short period of time, 4 to 5 hours and that atmospheric pressure can be used, eliminating the need for a costly vacuum system.