Protective conversion coating on mixed-metal substrates and methods thereof
AssigneeThe Curators of the University of Missouri
InventorsMatthew J. O'Keefe, Surender Maddela
Life of this patent
Estimating the term…
Abstract
Mixed-metal automotive vehicle bodies-in-white comprising ferrous metal surfaces, zinc surfaces, aluminum alloy surfaces, and magnesium alloy surfaces are cleaned and immersed in an aqueous bath comprising an adhesion promoter and an aqueous electrocoat bath (the adhesion promoter may be in the electrocoat bath. The adhesion promoter, which may be a cerium salt, is selected to react with each metal in the body surfaces to form an oxide layer that provides corrosion resistance for the surface and adherence for the deposited polymeric paint coating. The body is cathodic in the electrocoat deposition.
Claims18
A method of forming a protective conversion coating on a mixed-metal substrate, the method comprising:
- contacting a cerium salt and an oxidizing agent, sufficient to form a protective conversion coating solution;
- providing a mixed-metal substrate having a plurality of joined metal surfaces, at least one of the surfaces comprising magnesium, and at least one of the surfaces comprising ferrous metal, zinc, or aluminum;
- and
- depositing the protective conversion coating solution on each metal surface of the mixed-metal substrate to form a protective metal coating conversion solution layer, and wherein any metal present is selected from the group consisting of cerium and one or more metals of the mixed-metal substrate.
A method of forming a protective conversion coating on a mixed-metal substrate, the method comprising:
- providing a mixed-metal substrate having a plurality of joined metal surfaces, at least one surface comprising magnesium, and at least one of the surfaces comprising ferrous metal, zinc, or aluminum;
- immersing the mixed-metal substrate in an aqueous bath including a dissolved oxidizing composition comprising metal cations capable of forming a conversion coating with each metal surface of the mixed-metal substrate;
- wherein the metal cations are selected from a group consisting of cerium cations, the conversion coating includes cerium and oxygen, and the metal cations react with each of the metal surfaces of the mixed-metal substrate upon immersion to form a conversion coating on each metal surface of the mixed-metal substrate.
A method of forming a protective conversion coating on a mixed-metal substrate, the method comprising:
- providing a mixed-metal substrate having a plurality of joined metal surfaces including a first surface comprising magnesium, and a second metal surface different from the first surface;
- and
- immersing the mixed-metal substrate in an aqueous bath including a dissolved oxidizing composition comprising cerium cations capable of forming a conversion coating with each metal surface of the mixed-metal substrate, wherein the conversion coating includes cerium and oxygen, and the cerium cations react with each of the metal surfaces of the mixed-metal substrate upon immersion to form a conversion coating on the surface of each metal of the mixed-metal substrate.
A method of forming a protective conversion coating on a mixed-metal substrate, the method comprising:
- contacting a cerium salt and an oxidizing agent, sufficient to form a protective conversion coating solution;
- providing a mixed-metal substrate having a plurality of joined metal surfaces including a first surface comprising magnesium, and a second metal surface different from the first surface;
- and
- depositing the protective conversion coating solution on each metal surface of the mixed-metal substrate to form a protective coating conversion solution layer;
- wherein the conversion coating solution comprises an accelerator selected from the group consisting of a peroxide compounds.
Dependencies are inferred from the claim text.