Ceramic proppants
AssigneeShamrock Group
InventorsFrank O'Brien, Chris Heller
Life of this patent
Estimating the term…
Abstract
A sintered, generally spherical ceramic body, having an alumina content of from about 52 to about 55 weight percent distributed substantially homogeneously throughout the body, a silica content from about 32 to about 38 weight percent distributed substantially homogeneously throughout the body, an apparent specific gravity of about 2.61 to about 2.65, and a bulk density of about 1.45 to about 1.56 grams per cubic centimeter.
Claims1
A high strength propping agent for use in hydraulic fracturing of subterranean formations comprising a plurality of solid, substantially spherical particles, wherein the particles are characterized by a specific gravity of between 2.61 and 2.65 grams per cubic centimeter and ambient temperature permeability of at least about 100,000 millidarcies at 8,000 psi;
- wherein the composition of the particles comprises:
- about 36 weight percent alumina, about 56 weight percent silica, about 3 weight percent iron oxide, and about 2 weight percent titania, with the remainder being alkali and alkaline earth metal oxides.
Dependencies are inferred from the claim text.