Method of manufacturing multilayer electrolyte reinforced composite membrane
AssigneeHyundai Motor Company
InventorNak Hyun Kwon
Life of this patent
Estimating the term…
Abstract
The present invention relates to a method of manufacturing a multilayer electrolyte reinforced composite membrane that is mechanically stable and cost-efficient and has superior hydrogen ion conductivity even when exposed to low humidity and high temperature conditions. The method of the invention involves a stretching process and a series of drying steps to provide a hydrogen ion exchange membrane of a three-layer structure comprising: a matrix layer of a hydrogen ion exchange membrane impregnated and stretched with a polymer electrolyte sandwiched between two electrolyte coated layers.
Claims11
A method of manufacturing an electrolyte reinforced composite membrane with a multilayer comprising:
- stretching a porous film bidirectionally over the whole area;
- coating and impregnating the stretched film with an electrolyte solution, drying the resulting film at about 80-130° C. and stretching the dried film wherein said coating and impregnating, drying and stretching are processed successively about two to ten times to form a matrix layer and said film is stretched uniformly and bidirectionally over the whole area while coating and impregnating and stretched while drying;
- coating the upper and lower portions of the matrix layer with the electrolyte solution and drying the matrix layer at about 100-150° C. to form an electrolyte coated layer;
- and
- hot-pressing the electrolyte coated layer at about 120-150° C.
A method of manufacturing an electrolyte reinforced composite membrane with a multilayer comprising:
- coating and stretching a porous film bidirectionally over the whole area;
- coating and impregnating the stretched film with an electrolyte solution, drying the resulting film at about 80-130° C. and stretching the dried film wherein said coating and impregnating, drying and stretching are processed successively about two to ten times to form a matrix layer and said film is stretched uniformly and bidirectionally over the whole area while coating and impregnating and stretched while drying;
- coating the upper and lower portions of the matrix layer with the electrolyte solution and drying the matrix layer at about 100-150° C. to form an electrolyte coated layer;
- and
- hot-pressing the electrolyte coated layer at about 120-150° C.,
- wherein said porous film is expanded polytetrafluoroethylene (e-PTFE) film and said electrolyte is a perfluorosulfonated ionomer or a mixture comprising a perfluorosulfonated ionomer and a heteropoly acid, and
- said matrix layer and said electrolyte coated layer have a 3 layer structure according to (a), (b) or (c);
- (a) a perfluorosulfonated ionomer layer as the electrolyte coated layer/e-PTFE film impregnated with perfluorosulfonated ionomer as the matrix layer/perfluorosulfonated ionomer layer as the electrolyte coated layer,
- (b) a mixture layer of a perfluorosulfonated ionomer and a heteropoly acid as the electrolyte coated layer/e-PTFE film impregnated with a mixture of a perfluorosulfonated ionomer and a heteropoly acid as the matrix layer/a mixture layer of a perfluorosulfonated ionomer and a heteropoly acid as the electrolyte coated layer, or
- (c) a perfluorosulfonated ionomer layer as the electrolyte coated layer/e-PTFE film impregnated with a mixture of a perfluorosulfonated ionomer and a heteropoly acid as the matrix layer/perfluorosulfonated ionomer layer as the electrolyte coated layer.
A method of manufacturing an electrolyte reinforced composite membrane with a multilayer comprising:
- stretching a porous film bidirectionally over the whole area;
- coating and impregnating the stretched film with an electrolyte solution, drying the resulting film at about 80-130° C. and stretching the dried film wherein said coating and impregnating, drying and stretching are processed successively and said film is stretched uniformly and bidirectionally over the whole area while coating and impregnating and stretched while drying;
- and
- coating the upper and lower portions of the matrix layer with the electrolyte solution and drying the matrix layer at about 100-150° C. to form an electrolyte coated layer.
Dependencies are inferred from the claim text.