Method of continuous casting of high-aluminum steel and mold powder

A method of continuous casting a molten steel in a mold using a mold powder while controlling molten steel surface level fluctuation speed, mold oscillation stroke amplitude while pouring the molten steel, and negative strip time tN, wherein the molten steel contains 0.1 to 3.0% (% by mass, hereinafter the same) of Al and also each 4.0% or less (excluding 0%) of Si, Mn, Ni, Cr, and Mo and C in a content [C] satisfying relations defined by the following expressions (1) to (3):

• f1−0.10≦[C]+0.05 (1);
• f1=0.0828[Si]−0.0195[Mn]+0.07398[Al]−0.04614[Ni]+0.02447[Cr]+0.01851[Mo]+0.090 (2);
• and
• f2=0.2187[Si]−0.03291[Mn]+0.2017[Al]−0.06715[Ni]+0.04776[Cr]+0.04601[Mo]+0.173 (3)
• wherein [Si], [Mn], [Al], [Ni], [Cr], and [Mo] denote respective contents (% by mass) of Si, Mn, Ni, Cr, and Mo), wherein
• said mold powder contains T—CaO:
• 35 to 55%, SiO2:
• 10 to 30%, Al2O3:
• 4.0% or less (excluding 0%), MgO:
• 0.2 to 1.0%, Li2O:
• 7 to 13%, F:
• 7 to 13%, C, 10.5 to 14%, and inevitable impurities and satisfies the following expressions (4) and (5):
• 1.6≦[T—CaO]/[SiO2]≦5 (4);
• and
• 0.2≦[Li2O]/[SiO2]≦1.1 (5)
• wherein [T—CaO], [SiO2], and [Li2O] denote respective contents (% by mass) of T—CaO, SiO2, and Li2O in the mold powder and T—CaO is the amount of CaO (% by mass) in the mold powder when the total amount of Ca in the mold powder is converted into CaO;
• and the method is carried out by
• adjusting the molten steel surface level fluctuation speed in the mold to 14 mm/second or lower;
• pouring the molten steel in the width direction of the mold using an immersion nozzle at a pouring angle of 0° or more and 55° or less downward from the horizontal direction while applying mold oscillation in the condition of the stroke in the amplitude from greater than 2 mm to no greater than 8 mm and the negative strip time tN defined by the following expression (6) of 0.28 seconds or shorter:
• tN=(1/π·f)cos−1(Vc/π·f·s) (6)
• wherein f denotes the mold oscillation frequency (Hz);
• s denotes the distance (mm) between the upper dead point and the lower dead point of the mold at the time of mold oscillation;
• and Vc denotes the casting velocity (mm/s) of a slab.