Abstract
The present invention relates to a novel electrical devices fabricated from polycrystalline silicon carbide (SiC) and methods for forming the same. The present invention provides a method for fabricating polycrystalline silicon carbide (SiC) products infiltrated with SiC-containing preceramic precursor resins to substantially mask the deleterious effects of trace contaminants, typically nitrogen and aluminum, while reducing operative porosity and enhancing manufacturing ease.
Claims2
A method for manufacturing an impregnated silicon carbide (SiC) hot surface igniter body from polycrystalline silicon carbide, comprising the steps of:
- forming a slip cast SiC ceramic body;
- drying the slip cast SiC ceramic body to thereby form a porous green body having open porosity;
- vacuum-pressure impregnating said green body with an allylhydridopolycarbosilane (AHPCS) resin;
- curing the impregnated ceramic body at a peak temperature between approximately 250° C. to 450° C. in an inert atmosphere;
- slicing and slotting the cured impregnated body with a manufacturer-selected igniter shape;
- pyrolyzing the cured and impregnated ceramic body at a temperature as low as 650° C. in an inert atmosphere to form a ceramic-bonded particulate SiC ceramic composite bisque product, thereby forming a permanent bonding amorphous phase at temperatures as low as 650° C. enabling an improved process strength;
- the pyrolized ceramic body having a first wide cross-section portion and a second narrow cross-section portion perpendicular to the first cross-section;
- orienting said pyrolized ceramic body in a recrystallization furnace in a first orientation with said first wide cross-section portion parallel to the field of gravity;
- recrystallizing said pyrolized ceramic body at a minimum temperature of 1800° C. in an inert gas atmosphere, whereby said amorphous phase enables said recrystallization step without orienting said first wide cross-section portion perpendicular to said field of gravity;
- and
- wherein said step of orienting further comprises the steps of:
- positioning a plurality of pyrolized ceramic bodies in said first orientation whereby respective said first wide cross-section portions contact respective first wide cross-section portions of adjacent pyrolized ceramic bodies prior to said step of recrystallizing.
A process for manufacturing an impregnated silicon carbide (SiC) hot surface igniter body from polycrystalline SiC comprising the steps of:
- forming a slip cast ceramic body comprising SiC particles;
- drying said slip cast SiC ceramic body to form a porous ceramic body having an open porosity and impregnating said porous ceramic body with an allylhydridopolycarbosilane (AHPCS) resin;
- curing the impregnated ceramic body at a peak temperature between approximately 250° C. to 400° C.;
- slicing and slotting the cured impregnated body into a manufacturer-selected igniter
- pyrolizing the cured and impregnated ceramic body at a temperature as low as 650° C. in an inert atmosphere to form a ceramic-bonded particulate ceramic composite body with all the pores rendered unavailable to such an extent that pore entry is prohibited, whereby said step of pyrolyzing forms a permanent amorphous SiC bonding phase at temperatures as low as 650° enabling an improved operational strength within a pre-recrystallization temperature range of between 650° C. and 2000° C.;
- conducting at least one repetition of said steps of impregnating, curing, and pyrolyzing whereby said ceramic body increases in density at each said repetition;
- said AHPCS resin is at least one of a group consisting of:
- a suspension formed by adding at least one of alumina or aluminum particles in an allylhydrido-polycarbosilane AHPCS resin prior to said step of infiltrating;
- an admixture suspension of a compatible organo-aluminum compound with a AHPCS resin;
- and a resin formed by incorporating aluminum compounds onto a backbone of an AHPCS resin polymer itself;
- and
- recrystallizing the pyrolized ceramic body at a minimum temperature of 1800° C. in an inert gas atmosphere.
Dependencies are inferred from the claim text.