Method for forming a tight-fitting silver surface on an aluminium piece
AssigneeOutotec Oyj
InventorsVeikko Polvi, Karri Osara
Life of this patent
Estimating the term…
Abstract
The invention relates to a method for forming a highly electroconductive surface on an aluminum piece. A highly conductive layer of silver is formed on the piece by means of a eutectic join. The temperature of the aluminum piece is raised gradually and the oxide layer formed on the surface of the piece is removed. After the first heating stage, the silver piece that is to be attached is transferred to the cleaned surface. The contact point is heated to a temperature where a eutectic bond is generated between the aluminum and silver. During the second heating stage a slight momentary loading is applied to the contact point.
Claims16
A method for forming a highly electroconductive silver coating on the surface of an aluminum piece, there being an oxide layer on the surface of the aluminum piece, and the method comprising:
- removing the oxide layer from the surface of the aluminum piece,
- heating the aluminum piece in a first stage,
- cleaning the surface of the aluminum piece after the first heating stage in order to remove any oxide layer formed on said surface after removing the oxide layer before the first heating stage,
- after the first heating stage, placing a silver piece in contact with a surface of the aluminum piece,
- heating the aluminum piece and the silver piece in contact therewith in a second stage at least to the temperature required for the eutectic reaction between aluminum and silver, the heating taking place under slightly reductive conditions, and
- during the second heating stage, pressing the silver piece against the aluminum piece by cyclically applying a load in the order of 0.2-3 bar to an area of the silver piece that is smaller than the silver piece.
A method for forming a highly electroconductive silver coating on the surface of an aluminum piece, there being an oxide layer on the surface of the aluminum piece, and the method comprising:
- providing a silver piece distinct from the aluminum piece,
- removing the oxide layer from the surface of the aluminum piece,
- heating the aluminum piece in a first stage after removing the oxide layer,
- after the first heating stage, placing the silver piece in contact with a surface of the aluminum piece,
- heating the aluminum piece and the silver piece in contact therewith in a second stage at least to the temperature required for the eutectic reaction between aluminum and silver, and
- during the second heating stage, pressing the silver piece against the aluminum piece by cyclically applying a load in the order of 0.2-3 bar to an area of the silver piece that is smaller than the silver piece.
Dependencies are inferred from the claim text.