Abstract
An additive for internal addition, which improves the paper qualities of a pulp sheet, such as stiffness and bulk which includes a polymer emulsion containing a natural cationic polymer (A) or synthetic cationic polymer (A′) and polymer particles (B) containing vinyl monomer-derived structural units.
Claims9
A method of making paper comprising:
- mixing a pulp slurry and a polymer emulsion comprising a cationic starch having a nitrogen content (N %) of 0.2 to 0.8 percent (A) and polymer particles (B) having an average particle diameter of 0.2 to 19.4 μm and comprising at least vinyl monomer-derived structural units comprising 94.66 wt. % to 100 wt. % of vinyl acetate units,
- wherein the polymer particles (B) are obtained by an emulsion polymerization method, suspension polymerization method or dispersion polymerization method in the presence of said cationic starch having a nitrogen content (N %) of 0.2 to 0.8 percent (A) to form a mixture, such that the proportion of (A) is from 10 to 315 parts by weight relative to 100 parts by weight of the polymer particles (B);
- wherein the polymer emulsion has a solid content of 7.9 to 39% by weight and wherein the glass transition temperature (TG) of (B) is from 32° C. to 59° C.;
- filtering said mixture on a wire mesh to drain water out to form a paper layer,
- wherein said polymer emulsion is added to said pulp slurry at the time of papermaking, and
- wherein the emulsion polymerization method, suspension polymerization method or dispersion polymerization method is carried out in the presence of a surfactant.
3 more elements
A method of making paper comprising:
- mixing a pulp shiny and a polymer emulsion comprising a cationic starch having a nitrogen content (N %) of 0.2 to 0.8 percent (A) having a viscosity of 20 mPa·s or more in a 7 wt. % aqueous solution as determined at 50° C. with a Brookfield viscometer and Rotor No. 2 at 60 rpm, and polymer particles (B) having an average particle diameter of 0.2 to 19.4 μm and having a glass transition temperature (TG) of 32° C. to 59° C. having vinyl monomer-derived structural units comprising 94.66 wt. % to 100 wt. % of vinyl acetate units,
- wherein the polymer particles (B) are obtained by an emulsion polymerization method, suspension polymerization method or dispersion polymerization method in the presence of said cationic starch having a nitrogen content (N %) of 0.2 to 0.8 percent (A), such that the proportion of (A) is from 10 to 315 parts by weight relative to 100 parts by weight of the polymer particles (B);
- and wherein the polymer emulsion has a solid content of 7.9 to 39% by weight;
- filtering said mixture on a wire mesh to drain water out to form a paper layer,
- wherein said polymer emulsion is added to said pulp slurry at the time of papermaking, and
- wherein the emulsion polymerization method, suspension polymerization method or dispersion polymerization method is carried out in the presence of a surfactant.
3 more elements
A method of improving stiffness of paper comprising:
- bringing pulp into contact with a polymer emulsion comprising a cationic starch having a nitrogen content (N %) of 0.2 to 0.8 percent (A) and polymer particles (B) having an average particle diameter of 0.2 to 19.4 μm and comprising at least vinyl monomer-derived structural units comprising 94.66 wt. % to 100 wt. % of vinyl acetate units,
- wherein the polymer particles (B) are obtained by an emulsion polymerization method, suspension polymerization method or dispersion polymerization method in the presence of said cationic starch having a nitrogen content (N %) of 0.2 to 0.8 percent (A), such that the proportion of (A) is from 10 to 315 parts by weight relative to 100 parts by weight of the polymer particles (B);
- wherein the polymer emulsion has a solid content of 7.9 to 39% by weight;
- and wherein the glass transition temperature (TG) of (B) is from 32° C. to 59° C.;
- wherein said pulp is contacted with said polymer emulsion at the time of papermaking, and
- wherein the emulsion polymerization method, suspension polymerization method or dispersion polymerization method is carried out in the presence of a surfactant.
3 more elements
Dependencies are inferred from the claim text.