US 7,677,297 B2 · Reducing residual stresses during sand casting

Abstract

Residual stress is reduced in light metal alloy articles, e.g. aluminum alloy articles, formed as castings against a sand casting mold body by incorporating a wax composition of suitable softening or melting temperature with the sand particles of the mold or core body. The hot cast metal heats adjoining surfaces of the mold body. As the cooling metal forms a solid shell, the surrounding sand particle and wax mixture are heated sufficiently to melt or soften the wax incorporated on or between sand particles. This softens portions of the rigid mold body that could otherwise restrain shrinking surfaces of the casting and produce unwanted stressed regions that are retained in the casting and must be removed by subsequent processing.

Claims18

Dependent claims

A method of making a sand particle-containing mold body for casting articles of light metal alloys where article-shaping surfaces of the mold body are heated by the cast metal and at least a portion of the surface of the cast article shrinks against an article-shaping surface of the mold body as the cast metal solidifies and cools, the method comprising:

identifying a region of the mold body wherein a surface of the cast article may shrink against a portion of the article-shaping surface of the mold body during solidification of cast light metal alloy and sustain residual compressive or tensile stresses in that surface of the cast article;
selecting a wax composition and amount for mixing with sand particles used in making at least the identified region of the mold body, the wax composition and amount being selected to soften the identified region after an initial solidified shell of the cast article has formed during solidification of the casting and to reduce compressive or tensile stresses in the surface region of the cast article shrinking against the article-shaping surface of the mold, the amount of wax in the identified region being up to the weight of the sand particles;
and
mixing the selected wax composition and amount with sand particles in forming at least the identified region of the mold.

1 more element

A method of making an article of a light metal alloy by casting a melt of the light metal alloy against an article shape-defining surface of a sand particle-containing mold body where a surface of the cast article shrinks against an article shape-defining surface of the mold body as the cast metal forms an initial solidified shell and then fully solidifies and cools, the method comprising:

identifying a region of the mold body wherein a surface of the cast article may shrink against a portion of the article-shaping surface of the mold body during solidification of cast light metal alloy and sustain residual compressive or tensile stresses in that surface of the cast article;
making the mold body in which at least the identified region of whole mold body is made with a mixture comprising a wax composition and sand particles, the sand particles initially consisting essentially of sand, clay, and moisture for bonding as a mold body, the wax composition and its amount being selected by experimentation to soften after an initial solidified shell of the cast article has formed during solidification of the casting and to reduce compressive or tensile stresses in the surface region of the cast article shrinking against the article shape-defining surface of the mold;
pouring a melt of the light metal alloy against the mold body, the mold body initially being at an ambient temperature;
allowing the cast metal article to solidify and cool against the mold body surface;
and, when the cast article has reached a suitable temperature for removal from contact with the mold body,
removing the cast article from the mold body, the cast article having lower residual compressive or tensile stresses due to the softening of the wax composition.

3 more elements

Dependencies are inferred from the claim text.

Reducing residual stresses during sand casting

Life of this patent

Reducing residual stresses during sand casting

Life of this patent

Abstract

Claims18