Laminated polyester film and manufacturing process thereof
AssigneeTeijin Dupont Films Japan Limited
InventorsShinji Yano, Atsushi Oyamatsu
Life of this patent
Estimating the term…
Abstract
A laminated polyester film comprising a coating layer formed on at least one side of a polyester film, this coating layer comprising a polymer binder and inorganic-organic composite particles having an average particle diameter of 200 to 2,000 nm. This film has excellent scratch resistance, adhesion, transparency and slipperiness and is useful as an adhesive film for optical use.
Claims3
A laminated polyester film comprising:
- (A) a polyester film;
- and
- (B) a 0.04 to 0.5 microns thick coating layer formed on at least one side of the polyester film (A) and made of a coating composition comprising 5 to 95 wt % polyester resin having a glass transition point of 60 to 80° C., 5 to 95 wt % of an acrylic resin having an oxazoline group and a polyalkylene oxide chain and inorganic-organic composite particles having an average particle diameter of 300 to 1500 nm and containing 10 to 40 wt % of elemental silicon and wherein the composite particles are present in an amount of 0.01 to 5 parts by weight based on 100 parts by weight of the coating composition of the coating layer.
A process of manufacturing a laminated polyester film, comprising the steps of:
- applying an aqueous coating solution to at least one side of a polyester film before the completion of crystal orientation of the polyester film;
- and
- stretching the coated film in at least one direction and heat setting it to form a coating layer on at least one side of the stretched polyester film,
- wherein the aqueous coating solution yields the coating layer which is 0.04 to 0.5 microns thick and is made of a coating composition comprising 5 to 95 wt % polyester resin having a glass transition point of 60 to 80° C., 5 to 95 wt % of an acrylic resin having an oxazoline group and a polyalkylene oxide chain and inorganic-organic composite particles having an average particle diameter of 300 to 1500 nm and containing 10 to 40 wt % of elemental silicon and wherein the composite particles are present in an amount of 0.01 to 5 parts by weight based on 100 parts by weight of the coating composition of the coating layer.
1 more element
Dependencies are inferred from the claim text.