Polysilicon dummy wafers and process used therewith

Abstract

Non-production wafers of polycrystalline silicon are placed in non-production slots of a support tower for thermal processing monocrystalline silicon wafers. They may have thicknesses of 0.725 to 2 mm and be roughened on both sides. Nitride may be grown on the non-production wafers to a thickness of over 2 μm without flaking. The polycrystalline silicon is preferably randomly oriented Czochralski polysilicon grown using a randomly oriented seed, for example, CVD grown silicon. Both sides are ground to introduce sub-surface damage and then oxidized and etch cleaned. An all-silicon hot zone of a thermal furnace, for example, depositing a nitride layer, may include a silicon support tower placed within a silicon liner and supporting the polysilicon non-production wafers with silicon injector tube providing processing gas within the liner.