Defectivity and process control of electroless deposition in microelectronics applications
AssigneeEnthone Inc.
InventorsQingyun Chen, Charles Valverde, Vincent Paneccasio, Nicolai Petrov, Daniel Stritch, Christian Witt, Richard Hurtubise
Life of this patent
Estimating the term…
Abstract
Methods and compositions for electrolessly depositing Co, Ni, or alloys thereof onto a substrate in manufacture of microelectronic devices. Grain refiners, levelers, oxygen scavengers, and stabilizers for electroless Co and Ni deposition solutions.
Claims4
An electroless deposition composition for electrolessly depositing Co, Ni, or alloys thereof onto a substrate in manufacture of microelectronic devices, the deposition composition comprising (a) a source of deposition ions selected from the group consisting of Co ions and Ni ions, (b) a reducing agent for reducing said deposition ions onto the substrate, and (c) a stabilizer comprising a molybdenum oxide;
- wherein the molybdenum oxide is selected from the group consisting of MoO3 predissolved with TMAH;
- (NH4)2MoO4;
- and a combination thereof;
- and
- wherein the stabilizer is present in the electroless deposition composition at a concentration between about 10 ppm and about 800 ppm.
An electroless deposition composition for electrolessly depositing Co, Ni, or alloys thereof onto a substrate in manufacture of microelectronic devices, the deposition composition comprising (a) a source of deposition ions selected from the group consisting of Co ions and Ni ions, (b) a reducing agent for reducing said deposition ions onto the substrate, and (c) a stabilizer comprising a molybdenum oxide;
- wherein the molybdenum oxide is selected from the group consisting of (NH4)2Mo2O7;
- dimolybdates (Me2Mo2O7.nH2O);
- metamolybdates (Me2H10−m[H2(Mo2O7)6].nH2O);
- and combinations thereof;
- wherein Me is a counterion selected from among ammonium, tetramethylammonium, and alkali metal cations;
- m is less than 10;
- and n is an integer having a value corresponding to a stable or metastable form of the hydrated oxide;
- wherein the stabilizer is present in the electroless deposition composition at a concentration between about 10 ppm and about 800 ppm.
An electroless deposition composition for electrolessly depositing Co, Ni, or alloys thereof onto a substrate in manufacture of microelectronic devices, the deposition composition comprising (a) a source of deposition ions selected from the group consisting of Co ions and Ni ions, (b) a reducing agent for reducing said deposition ions onto the substrate, and (c) a stabilizer comprising a vanadium oxide, wherein the vanadium oxide is pyrovanadates (V2O74−).
An electroless deposition composition for electrolessly depositing Co, Ni, or alloys thereof onto a substrate in manufacture of microelectronic devices, the deposition composition comprising (a) a source of deposition ions selected from the group consisting of Co ions and Ni ions, (b) a reducing agent for reducing said deposition ions onto the substrate, and (c) a stabilizer comprising a molybdenum oxide;
- wherein the molybdenum oxide is a dimolybdate (Me2Mo2O7.nH2O), wherein Me is ammonium;
- and
- wherein the stabilizer is present in the electroless deposition composition at a concentration between about 10 ppm and about 800 ppm.
Dependencies are inferred from the claim text.