Oil tempered wire for cold forming coil springs

Abstract

An oil-tempered wire for a cold-formed coil spring having a quality equivalent of or higher than a hot-formed coil spring is provided. A cold-formed coil spring made from the oil-tempered wire is also provided. Material used is the steel which contains, in weight percentage, 0.35 to 0.55% C, 1.8 to 3.0% Si, 0.5 to 1.5% Mn, 0.5 to 3.0% Ni, and 0.1 to 1.5% Cr. The ferrite fraction in the microscopic structure of this material is set to 50% or less. Hot rolled wire is cold drawn with a predetermined reduction of area, and a heat treatment using high frequency induction heating is conducted. It is preferable to set the maximum heating temperature between 900° C. to 1020° C. (favorably 950° C.) and holding time between 5 to 20 seconds. It is preferable to make the oil tempered material to have the grain size number of 9 or more, and the tensile strength from 1830 to 1980 MPa.