Method for high aspect ratio pattern transfer
AssigneeNational Cheng Kung University
InventorsWeng-Chung Liao, Lien-Chung Hsu, Po-I Lee, Min-Hsiung Hon, Chau-Nan Hong
Life of this patent
Estimating the term…
Abstract
The present invention relates a method for high aspect ratio pattern transfer, by using combination of imprint and Step and Flash techniques to transfer high aspect ratio pattern. The present invention simultaneously saves the developing time and the amount of developer used during the photo-resist pattern transfer process. The present invention is able to avoid separation and dissolution between pattern and substrate that is attacked by developer, and is able to yield high aspect ratio patterns.
Claims6
A method for high aspect ratio pattern transfer of positive photoresist application comprising the steps of:
- (1) obtaining a moldboard being pervious to light and having a protruding-and-recessing figure and forming a masking layer by way of sputtering deposition of a masking material on said moldboard;
- (2) after solidifying said masking layer, grinding the masking layer on the protruding part of said figure of said moldboard making said protruding part pervious to light;
- (3) obtaining a substrate applied with positive photoresist and then urging the mold at a molding pressure into the film creating a thickness contrast pattern in the film, wherein the molding pressure is sufficiently high to transfer the features to the film and the molding pressure causes a local deformation in the mold which is less than the mold pattern lateral dimension with said substrate that has said protruding-and-recessing figure for further processing Step and Flash;
- (4) after finishing said Step and Flash process, removing said moldboard from said substrate;
- and
- (5) with a developer, washing exposed portions of the thin film covered with said positive photoresist on said substrate to show the unexposed portion whereby produces high aspect ratio pattern.
A method for high aspect ratio pattern transfer of negative photoresist application comprising the steps of:
- (1) obtaining a moldboard being pervious to light and having a protruding-and-recessing figure and forming a masking layer by way of sputtering deposition of a masking material on said mold board;
- (2) after solidifying the masking layer, grinding a portion of the protruding-and-recessing figure making a remaining portion of the protruding-and-recessing figure pervious to light;
- (3) obtaining a substrate and depositing negative photoresist on said substrate;
- (4) covering said moldboard with said substrate that has said protruding-and-recessing figure for further processing Step and Flash from the said moldboard side;
- (5) after finishing said Step and Flash process, removing said moldboard from said substrate;
- and
- (6) with developer, washing unexposed portions of the thin film covered with said negative photoresist on said substrate to show the exposed portion whereby produces high aspect ratio pattern.
Dependencies are inferred from the claim text.