Pattern formation method
AssigneeMatsushita Electric Industrial Co., Ltd.
InventorsMasayuki Endo, Masaru Sasago
Life of this patent
Estimating the term…
Abstract
After forming a resist film from a positive chemically amplified resist material, an insolubilization treatment for making the surface of the resist film insoluble in a developer is carried out. After the insolubilization treatment, pattern exposure is performed by selectively irradiating the resist film with exposing light. Thereafter, the resist film is developed so as to form a resist pattern made of an unexposed portion of the resist film.
Claims4
A pattern formation method comprising the steps of:
- (a) forming a resist film from a positive chemically amplified resist material;
- (b) performing an insolubilization treatment for making a surface of said resist film insoluble in a developer;
- (c) performing pattern exposure by selectively irradiating said resist film with exposing light after the insolubilization treatment;
- and
- (d) annealing said resist film after the pattern exposure;
- (e) forming a resist pattern made of an unexposed portion of said resist film by developing said resist film after step (d),
- wherein the insolubilization treatment includes a step of exposing the surface of said resist film to an alkaline aqueous solution, and
- said alkaline aqueous solution is a tetramethylammonium hydroxide aqueous solution or a choline aqueous solution.
A pattern formation method comprising the steps of:
- (a) forming a resist film from a positive chemically amplified resist material;
- (b) performing an insolubilization treatment for making a surface of said resist film insoluble in a developer;
- (c) performing pattern exposure by selectively irradiating said resist film with exposing light after the insolubilization treatment;
- and
- (d) annealing said resist film after the pattern exposure;
- and
- (e) forming a resist pattern made of an unexposed portion of said resist film by developing said resist film after step (d),
- wherein the insolubilization treatment includes a step of exposing the surface of said resist film to plasma.
A pattern formation method comprising the steps of:
- (a) forming a resist film from a positive chemically amplified resist material;
- (b) performing an insolubilization treatment for making a surface of said resist film insoluble in a developer;
- (c) performing pattern exposure by selectively irradiating said resist film with exposing light after the insolubilization treatment;
- and
- (d) annealing said resist film after the pattern exposure;
- and
- (e) forming a resist pattern made of an unexposed portion of said resist film by developing said resist film after step (d),
- wherein an acid generator included in said chemically amplified resist material is an onium salt, and
- said onium salt is triphenylsulfonium trifluoromethanesulfonate or triphenylsulfonium nonafluorobutanesulfonate.
Dependencies are inferred from the claim text.