Substituted phenylethylene precursor synthesis method
AssigneeSharp Laboratories of America, Inc.
InventorsWei-Wei Zhuang, Tue Nguyen, Lawrence J. Charneski, David R. Evans, Sheng Teng Hsu
Life of this patent
Estimating the term…
Abstract
A Cu(hfac) precursor with a substituted phenylethylene ligand has been provided. The substituted phenylethylene ligand includes bonds to molecules selected from the group consisting of C1 to C6 alkyl, C1 to C6 haloalkyl, C1 to C6 phenyl, H and C1 to C6 alkoxyl. One variation, the α-methylstyrene ligand precursor has proved to be stable a low temperatures, and sufficiently volatile at higher temperatures. Copper deposited with this precursor has low resistivity and high adhesive characteristics. A synthesis method has been provided which produces a high yield of the above-described precursor.
Claims2
A method for synthesizing a cooper(hfac) substituted phenylethylene precursor comprising the steps of:
- a) forming a uniformly mixed solution of Cu2O in a solvent;
- b) introducing a substituted phenylethylene to the solution of Step a), and forming a uniformly mixed solution;
- c) introducing hexafluoroacetylacetone (hfac) to the solution of Step b), and forming a uniformly mixed solution;
- d) filtering the solution to remove solid materials, where any excess Cu2O is removed;
- e) removing the solvent from the solution;
- f) stirring until any crystallized precursor in the solution is dissolved;
- g) letting the solution stand until crystals form;
- h) filtering to remove the solid material, whereby a liquid phase precursor is formed;
- and
- i) adding less than approximately 10% by weight ratio, of the substituted phenylethylene used in Step b) to the solution, whereby the liquid phase stability of the precursor is improved.
Dependencies are inferred from the claim text.