Method of fabricating a semiconductor device using trench isolation method including hydrogen annealing step
AssigneeSamsung Electronics Co., Ltd.
InventorsTai-su Park, Kyung-won Park, Jung-woo Park, Won-sang Song
Life of this patent
Estimating the term…
Abstract
A method of fabricating a semiconductor device using a trench isolation method including a hydrogen annealing step, wherein a photoresist pattern is formed on a semiconductor substrate, a pad insulating layer may be formed before forming the photoresist pattern, the semiconductor substrate is etched using the photoresist pattern as an etching mask to form a trench, and an isolation layer is formed in the trench. To remove damages created in an active region defined by the isolation layer, the semiconductor substrate having the isolation layer is annealed in a hydrogen atmosphere.
Claims12
A trench isolation method comprising:
- forming a trench in a semiconductor substrate including,
- forming a pad insulating layer on the semiconductor substrate,
- forming a photoresist pattern on the pad insulating layer, the photoresist
- pattern being formed to have a width of the isolation layer,
- etching the pad insulating layer and the semiconductor substrate using the
- photoresist pattern as a mask to form the trench in the semiconductor substrate, and
- removing the photoresist pattern;
- forming an isolation layer in the trench including,
- forming a thermal oxide film on the inner wall of the trench,
- forming a nitride liner on the thermal oxide film,
- forming a dielectric layer on the semiconductor substrate to fill the trench on which the nitride liner is formed,
- planarizing the surface of the semiconductor substrate having the dielectric layer using the nitride liner as a planarization stop layer by a chemical mechanical polishing method using a slurry containing abrasives of the ceria family,
- removing the nitride liner exposed by the planarization, and
- removing the pad insulating layer;
- and
- annealing the semiconductor substrate, having the isolation layer, in a hydrogen atmosphere.
A trench isolation method comprising:
- forming a trench in a semiconductor substrate;
- forming an isolation layer in the trench including,
- forming a thermal oxide film on the surface of the semiconductor substrate including the trench,
- forming a nitride liner on the thermal oxide film,
- forming a dielectric layer on the surface of the semiconductor substrate to fill the trench,
- planarizing the surface of the semiconductor substrate having the gap filling dielectric layer using the nitride liner as a planarization stop layer by a chemical mechanical polishing method using a slurry containing abrasives of the ceria family,
- removing the nitride liner acting as the planarization stop layer, and
- removing the thermal oxide film which is exposed by removal of the nitride liner;
- and
- annealing the semiconductor substrate, having the isolation layer, in a hydrogen atmosphere.