Coating for the working surface of the cylinders of combustion engines and a method of applying such a coating
AssigneeSulzer Metco AG
InventorGérard Barbezat
Life of this patent
Estimating the term…
Abstract
Ferrous coatings of the cylinder working surfaces of combustion engine blocks have a content of bound oxygen in the amount of between 1 to 4% by weight. They are characterized by extraordinary properties as far as tribology and the possibility of processing, e.g. machining, are concerned. Particularly, the coefficient of friction and the tendency to scuffing are substantially reduced. Such coatings can be realized, for example, by adding an amount of 200 to 1000 normalized liters air per minute during the plasma spraying operation.
Claims7
A ferrous coating applied by plasma spraying operation to a substrate serving as a cylinder working surface of a combustion engine block, said coating having a content of bound oxygen of between 1% and 4% by weight, said bound oxygen forming, together with iron, FeO and Fe3O4 crystals.
A ferrous coating applied by a plasma spraying operation to a substrate serving as a cylinder working surface of a combustion engine block, said coating have a content of bound oxygen of between 1% and 4% by weight, said bound oxygen forming together with iron, FeO and Fe3O4 crystals, wherein said substrate to which said coating is applied is constituted by a cylinder sleeve means made of cast iron and adapted to be inserted into an engine block made of a magnesium alloy or of an aluminum alloy.
A ferrous coating applied by a plasma spraying operation to a substrate serving as a cylinder working surface of a combustion engine block, said coating having a content of bound oxygen of between 1% and 4% by weight, said bound oxygen, forming together with iron, FeO and Fe3O4 crystals, said substrate to which said coating is applied being constituted by the engine block, said engine block being made of a magnesium alloy, of an aluminum alloy, or of cast iron, said cast iron being blended with compacted graphite.
A ferrous coating applied by a plasma spraying operation to a substrate serving as a cylinder working surface of a combustion engine block, said coating having a content of bound oxygen of between 1% and 4% by weight, said bound oxygen, forming together with iron, FeO and Fe3O4 crystals, said substrate to which said coating is applied being constituted by the engine block, said engine block being made of a magnesium alloy, of an aluminum alloy, or of cast iron, said cast iron being constituted by gray cast iron.
An apparatus comprising:
- a combustion engine block, said engine block including a cylinder working surface;
- and
- a ferrous coating applied by a plasma spraying operation to said cylinder working surface, said coating having a content of bound oxygen of between 1% and 4% by weight, said bound oxygen, forming together with iron, FeO and Fe3O4 crystals.