Conversion coatings on aluminum from KF solutions
AssigneeVisteon Global Technologies, Inc.
InventorsGerald Adam Grab, Kimberly A. Lazarz, Matthew John Zaluzec, Timothy Van Evans
Life of this patent
Estimating the term…
Abstract
The invention is a method of forming a conversion coating on an aluminum surface. According to the method, the aluminum surface is conversion coated by first treating the surface with thermal degreasing or aqueous alkaline degreasing and then contacting the treated surface with an aqueous bath solution of KF. The concentration of KF in the solution is 2.0-25.0 wt. % and the temperature is 90-212° F. for at least 5 seconds. The conversion coating consists essentially of: (a) substantially all K3AlF6 or (b) a mixture comprising a major proportion of K3AlF6 and a minor proportion of KAlF4
Claims15
A method for providing an abrasion resistant conversion coating on an aluminum surface of a swashplate for a swashplate compressor, comprising the steps of:
- (a) providing said aluminum surface which has been treated by thermal degreasing or aqueous alkaline degreasing to be substantially devoid of grease and oils;
- and
- (b) contacting the treated surface with an aqueous bath solution of 2.0-25.0 wt % KF at a temperature of 90° F.-212° F. for at least 5 seconds to provide a conversion coating on said surface consisting essentially of:
- (i) substantially all K3AlF6 or (ii) a mixture comprising a major proportion of K3AlF6 and a minor proportion of KAlF4.
A method for providing an abrasion resistant conversion coating on an aluminum surface, comprising the steps of:
- (a) providing said aluminum surface which has been treated by thermal degreasing or aqueous alkaline degreasing to be substantially devoid of grease and oils;
- (b) contacting the treated surface with an aqueous bath solution of 2.0-25.0 wt % KF at a temperature of 90° F.-212° F. for at least 5 seconds to provide a conversion coating on said surface consisting essentially of:
- (i) substantially all K3AlF6 or (ii) a mixture comprising a major proportion of K3AlF6 and a minor proportion of KAlF4;
- and
- (c) providing an adhesive on said conversion coated aluminum surface.
A method for providing an abrasion resistant conversion coating on a surface of an aluminum component, comprising the steps of:
- (a) treating said component with an alkaline cleaner to remove substantially all grease and oils from said component to form a treated surface;
- (b) contacting said treated surface with an aqueous bath solution of 2.0-25.0 wt % KF at a temperature of 90° F.-212° F. for 30-40 seconds to provide a conversion coating on said treated surface consisting essentially of:
- (i) substantially all K3AlF6 or (ii) a mixture comprising a major proportion of K3AlF6 and a minor proportion of KAlF4;
- (c) assembling said component into an apparatus that applies a frictional force against said conversion coating;
- and
- (d) said apparatus applying a frictional force against said conversion coating, whereby said conversion coating resists abrasion and wear.
A method for providing an abrasion resistant conversion coating on a surface of an aluminum swashplate, comprising the steps of:
- (a) treating said swashplate with an alkaline cleaner to remove substantially all grease and oils from said component to form a treated surface;
- (b) contacting said treated surface with an aqueous bath solution of 2.0-25.0 wt % KF at a temperature of 90° F.-212° F. for 30-40 seconds to provide a conversion coating on said treated surface consisting essentially of:
- (i) substantially all K3AlF6 or (ii) a mixture comprising a major proportion of K3AlF6 and a minor proportion of KAlF4;
- (c) assembling said swashplate into a compressor;
- (d) said compressor applying a frictional force against said conversion coating, whereby said conversion coating resists abrasion and wear.