Metals recovery system
AssigneeInternational Business Machines Corporation
InventorsJohn C. Kutt, Craig J. Gilmond, Jeff R. Kelby, Pat N. McCabe, Jr.
Life of this patent
Estimating the term…
Abstract
An evaporation system has fluorocarbon polymer-coated surfaces to permit easy removal of deposited metal. Evaporated lead-tin films will adhere strongly enough to a Teflon-coated shield so that the lead tin does not fall off during vacuum deposition but the bond between the lead-tin and the Teflon is still weak enough so that the lead-tin coating is easily peeled off, leaving the Teflon coating on the shield intact. The peeled lead-tin is substantially free of contamination so it can be reused, for example, in a subsequent deposition.
Claims18
A method of depositing material on a substrate, comprising:
- a) providing a deposition chamber comprising a chamber wall, a shield, and a source of the material to be deposited, wherein the shield is exposed to the deposited material, and further wherein the shield comprises a protective coating;
- b) depositing said material in said chamber wherein said deposited material adheres to said protective coating with sufficient adhesion to stick and wherein said deposited material adheres to said protective coating with adhesion sufficiently weak that said deposited material can be peeled off leaving said protective coating in place on the shield;
- c) peeling said deposited material from said protective coating on said shield;
- and
- d) re-using said peeled material without purification as said source of the material to be deposited.
A method of depositing material on a substrate, comprising the steps of:
- a) providing a vacuum deposition chamber and a source of a material, said material for depositing on the substrate in said chamber, said chamber comprising a chamber wall and a shield, wherein the shield is exposed to said material during operation of the system, and further wherein the shield comprises a protective coating;
- b) depositing said material in said chamber wherein said deposited material adheres to said protective coating with sufficient adhesion to stick without falling off during a vacuum deposition run and wherein said deposited material adheres to said protective coating with adhesion sufficiently weak that said deposited material can be peeled off leaving said protective coating in place on the shield;
- c) peeling said deposited material from said protective coating after said depositing step is complete, leaving said protective coating in place on the shield;
- and
- d) re-using said peeled material without purification as said source of the material to be deposited.
Dependencies are inferred from the claim text.