Methods of forming trench isolation regions using spin-on material
AssigneeVanguard International Semiconductor Corporation
InventorHorng-Huei Tseng
Life of this patent
Estimating the term…
Abstract
Disclosed are improved and simplified methods of forming trench isolation regions. A photoresist pattern having an opening therein is directly formed on a bare semiconductor substrate. The bare semiconductor substrate is etched through the opening in the photoresist pattern to form a trench in the substrate. The photoresist pattern is then isotropically etched to enlarge the size of the opening. A spin-on material layer is coated overlying the substrate surface to fill the trench and the enlarged opening, and then etched back until the photoresist pattern is exposed. After removing the photoresist pattern, the spin-on material layer is cured to form a trench isolation region which are less susceptible to edge defects.
Claims14
A method for forming a trench isolation region using spin-on material, comprising the steps of:
- forming a photoresist pattern directly on a bare semiconductor substrate, said photoresist pattern having an opening therein;
- etching the bare semiconductor substrate through the opening in said photoresist pattern, to form a trench in the substrate;
- enlarging the size of the opening in said photoresist pattern;
- coating a spin-on material layer in the trench and in the enlarged opening in the photoresist pattern;
- planarizing the spin-on material layer;
- removing the photoresist pattern from the bare semiconductor substrate;
- and
- curing the spin-on material layer to form a trench isolation region.
A method for forming a trench isolation region using spin-on material, comprising the steps of:
- forming an adhesive layer on a semiconductor substrate;
- forming a photoresist pattern having an opening therein on the adhesive layer, wherein the adhesive layer enhances adhesion between the substrate and the photoresist pattern;
- etching the adhesive layer and the semiconductor substrate through the opening in said photoresist pattern, to form a trench in the substrate;
- enlarging the size of the opening in said photoresist pattern;
- coating a spin-on material layer in the trench and in the enlarged opening in the photoresist pattern;
- planarizing the spin-on material layer;
- removing the photoresist pattern;
- and
- curing the spin-on material layer to form a trench isolation region.
Dependencies are inferred from the claim text.