Process for the production of high purity copper metal from primary or secondary sulphides
AssigneeEcochem Aktiengesellschaft
InventorGianni Zoppi
Life of this patent
Estimating the term…
Abstract
This process treats copper concentrates, either in the form of a primary sulfide, such as chalcopyrite, or a secondary sulfide, such as chalcocite and covellite, to obtain high purity copper metal having not less than 99.99% purity. In the case of a primary sulfide, the copper concentrate is subjected to leaching and is transformed into cement or a precipitated sulfide. In the case of the secondary sulfide, the copper concentrates are subjected to leaching with ferric fluoborate and fluoboric acid. Subsequent to leaching, the solution is subjected to copper electrowinning in a diaphragm cell to deposit copper on the cathode of the diaphragm cell.
Claims5
A process for obtaining purified copper metal from a copper concentrate comprising:
- (a) leaching chalcopyrite with cupric chloride to obtain a copper chloride solution according to equation (1), then separating elemental sulfur from the copper chloride solution, said equation (1) being as follows:
- 3CuCl.sub.2 +CuFeS.sub.2 .fwdarw.4CuCl+FeCl.sub.2 +2S.degree.(1);
- (b) reacting approximately one-fourth of the copper chloride solution obtained from said leaching (a) with either iron to precipitate a solid copper cement in accordance with equation (2a) or a sulfide to precipitate a copper sulfide precipitate in accordance with equation (2b), then filtering out the solid copper cement or the copper sulfide precipitate, said equations (2a) and (2b) being as follows:
- 2CuCl+Fe.fwdarw.2Cu+FeCl.sub.2 ( 2a),
- and
- 2CuCl+S.sup.2- .fwdarw.Cu.sub.2 S+2Cl.sup.- ( 2b);
- and
- (c) oxidizing approximately three-fourths of the copper chloride solution obtained from said leaching (a) to produce cupric chloride according to equation (3) and recycling the cupric chloride to said leaching (a), said equation (3) being as follows:
- 2CuCl+FeCl.sub.2 +3/4O.sub.2 +1/2H.sub.2 O.fwdarw.2CuCl.sub.2 +FeO.OH(3);
- (d) leaching the solid copper cement or the copper sulfide precipitate with ferric fluoborate and fluoboric acid to form a copper-containing solution by either reacting the solid copper cement obtained in (b) with ferric fluoborate and fluoboric acid in accordance with equation (4a) or reacting the copper sulfide precipitate obtained in (b) with ferric fluoborate and fluoboric acid in accordance with equation (4b), said equations (4a) and (4b) being as follows:
- 2Fe(BF.sub.4).sub.3 +Cu.fwdarw.2Fe(BF.sub.4).sub.2 +Cu(BF.sub.4).sub.2( 4a)
- 4Fe(BF.sub.4).sub.3 +Cu.sub.2 S.fwdarw.4Fe(BF.sub.4).sub.2 +2Cu(BF.sub.4).sub.2 ( 4b);
- and
- (e) electrowinning the copper-containing solution in a diaphragm cell having a cathode and an anode to deposit copper on the cathode in a purity of not less than 99.99% in accordance with equation 5(a), and to equation 5(b) at the anode, and overall equation (5) as follows:
- Cu(BF.sub.4).sub.2 +2e.fwdarw.Cu+2BF.sub.4.sup.- ( 5a),
- 2Fe(BF.sub.4).sub.2 +2BF.sub.4.sup.- .fwdarw.2Fe(BF.sub.4).sub.3 +2e(5b),
- and
- 2Fe(BF.sub.4).sub.2 +Cu(BF.sub.4).sub.2 .fwdarw.Cu+2Fe(BF.sub.4).sub.3( 5).
process for obtaining purified copper metal from a copper concentrate, said process comprising:
- leaching a secondary sulfide copper concentrate ore with ferric fluoborate and fluoboric acid to form a copper-containing solution in accordance with the following equations:
- CuS+2Fe(BF.sub.4).sub.3 .fwdarw.Cu(BF.sub.4).sub.2 +2Fe(BF.sub.4).sub.2 +S.degree.;
- and
- Cu.sub.2 S+4Fe(BF.sub.4).sub.3 .fwdarw.2Cu(BF.sub.4).sub.2 +4Fe(BF.sub.4).sub.2 +S.degree.;
- filtering the copper-containing solution to separate insoluble residues containing elemental sulfur and form a filtered solution;
- and
- electrowinning the filtered solution in the diaphragm cell having a cathode to deposit copper on the cathode in a purity of not less than 99.99%.
Dependencies are inferred from the claim text.