US 6,146,975 AGranted
Shallow trench isolation
AssigneeLucent Technologies Inc.
InventorsStephen Carl Kuehne, Alvaro Maury
Life of this patent
Estimating the term…
Abstract
The specification describes a dual patterned polish stop layer technique for shallow trench isolation. The shallow trenches are formed by etching trenches in a semiconductor substrate wafer, backfilling with oxide, and polishing by chemical-mechanical polishing (CMP) to produce a planar, trench isolated, wafer. To ensure planarity of the wafer after CMP, and avoid dishing of the field oxide, a dual silicon nitride polish stop layer is used. The first polish stop layer is applied selectively to protect the active device regions, and the second polish stop layer is applied selectively to protect the field oxide regions.
Claims12
A process for the manufacture of semiconductor integrated circuits comprising the steps of:
- a. depositing a first polish stop layer on a semiconductor substrate, said first polish stop layer comprising silicon nitride,
- b. masking first portions of said first polish stop layer with a first lithographic mask leaving second portions of said first polish stop layer exposed, said first portions being active device regions of said semiconductor substrate and said second portions being field oxide regions of said semiconductor substrate,
- c. etching the second portions of said first polish stop layer to form a patterned first polish stop layer,
- d. removing said first lithographic mask,
- e. etching the semiconductor substrate in said field oxide regions to form a plurality of trenches,
- f. depositing a gap filling dielectric on said semiconductor substrate, said gap filling dielectric covering said plurality of trenches and covering said patterned first polish stop layer,
- g. depositing a second polish stop layer on said gap filling dielectric, said second polish stop layer comprising silicon nitride,
- h. masking first portions of said second polish stop layer with a second lithographic mask, leaving second portions of said second polish stop layer exposed, said first portions of said second polish stop layer covering a major portion of said field oxide regions,
- i. etching said second portions of said second polish stop layer,
- j. removing said second lithographic mask,
- k. removing selected portions of said gap filling dielectric by chemical mechanical polishing, said selected portions being those portions of said gap filling dielectric covering said first polish stop layer, leaving said field oxide region.
8 more elements
A process for the manufacture of silicon integrated circuits comprising the steps of:
- a. growing a pad oxide layer on a silicon substrate,
- b. depositing a first silicon nitride layer on said pad oxide layer, said first silicon nitride layer having a thickness in the range 30-300 nm,
- c. masking first selected portions of said first silicon nitride layer with a first lithographic mask leaving second selected portions of said first silicon nitride layer exposed, said first selected portions being active device regions of said silicon substrate and said second selected portions being field oxide regions of said silicon substrate,
- d. etching the second selected portions of said first silicon nitride layer to form a patterned first silicon nitride layer and expose selected portions of said pad oxide layer,
- e. removing said first lithographic mask,
- f. etching the exposed selected portions of said pad oxide layer, leaving selected portions of said silicon substrate exposed,
- g. etching the exposed selected portions of said silicon substrate in said field oxide regions to form a plurality of trenches,
- h. depositing a gap filling dielectric on said silicon substrate to cover said trenches and cover said patterned first polish stop layer, said gap filling dielectric having a thickness T.sub.1,
- i. depositing a second silicon nitride layer on said gap filling dielectric,
- said second silicon nitride layer having a thickness T.sub.2,
- j. masking first selected portions of said second silicon nitride layer with a second lithographic mask, leaving second selected portions of said second silicon nitride layer exposed, said first selected portions covering a major portion of said field oxide regions,
- k. etching said second selected portions of said second silicon nitride layer,
- l. removing said second lithographic mask, and
- m. removing selected portions of said gap filling dielectric by chemical mechanical polishing with a selectivity S that removes said gap filling dielectric at a rate of S times the rate at which it removes said first silicon nitride layer and said second silicon nitride layer, and wherein S is .gtoreq.8 and is related to T.sub.1 and T.sub.2 by:
- T.sub.2 >T.sub.1 /S
- said selected portions of said fill oxide layer being those portions of said gap filling dielectric covering said first silicon nitride layer, leaving said field oxide regions.
13 more elements