Simplified shallow trench isolation formation with no polish stop
AssigneeAdvanced Micro Devices, Inc.
InventorsChristopher F. Lyons, Basab Bandyopadhyay, Nick Kepler, Olov Karlsson, Larry Wang, Effiong Ibok
Life of this patent
Estimating the term…
Abstract
An insulated trench isolation structure is formed in a semiconductor substrate omitting a barrier nitride polish stop layer, thereby simplifying the formation of the trench isolating structure, and enabling the substrate to be polished substantially flush with the trench fill. The planar trench fill-substrate interface avoids additional topography, thereby facilitating application of, and enhancing the accuracy of, photolithographic techniques in forming features with minimal dimensions.
Claims14
A method of manufacturing a semiconductor device having an insulated trench formed in a semiconductor substrate or in an epitaxial layer on said semiconductor substrate, which method comprises:
- forming a pad oxide layer on a main surface of said substrate or epitaxial layer;
- providing a photoresist mask directly on said pad oxide layer, said photoresist mask containing a pattern having an opening with a dimension substantially equal to a dimension of said trench;
- etching to remove portions of said underlying pad oxide layer and to form said trench having an internal surface;
- removing said photoresist mask;
- forming an oxide liner on said internal surface of said trench;
- depositing an insulating material directly on said pad oxide layer and to fill said trench;
- polishing such that said main surface is exposed and an uppermost surface of said insulating material is substantially coplanar with said main surface;
- and
- etching said main surface by wet etching or plasma etching subsequent to polishing.
A method of manufacturing a semiconductor device having an insulated trench formed in a semiconductor substrate or in an cpitaxial laver on said semiconductor substrate, which method comprises:
- forming a pad oxide layer on a main surface of said substrate or epitaxial layer;
- providing a photoresist mask directly on said pad oxide layer, said photoresist mask containing a pattern having an opening with a dimension substantially equal to a dimension of said trench;
- etching to remove portions of said underlying pad oxide layer and to form said trench having an internal surface;
- removing said photoresist mask;
- forming an oxide liner on said internal surface of said trench;
- depositing an insulating material directly on said pad oxide layer and to fill said trench;
- polishing such that said main surface is exposed and an uppermost surface of said insulating material is substantially coplanar with said main surface;
- forming an oxide repair layer on said main surface subsequent to polishing;
- and
- removing said repair layer by wet etching or plasma etching.
A method of manufacturing an integrated circuit on a semiconductor substrate, comprising:
- forming a silicon oxide pad layer on a main surface of said substrate or an epitaxial layer formed on said substrate;
- providing a photoresist mask directly on said pad oxide layer, said mask containing a pattern having an opening with a width substantially equal to a width of said trench of about 0.25.mu. or less;
- etching to remove portions of said underlying pad oxide layer and to form said trench, at a depth of about 2500 .ANG. to about 4000 .ANG., said trench having an internal surface;
- removing said mask;
- thermally growing a thin silicon oxide liner on said internal surface of said trench by heating to a temperature of about 1000.degree. C. or higher;
- depositing an insulating material directly on said pad oxide layer and to fill said trench, said insulating material comprising silicon dioxide derived from tetraethyl orthosilicate (TEOS) by low pressure chemical vapor deposition (LPCVD), silicon dioxide derived from silane by LPCVD, or a high density plasma oxide;
- chemical-mechanical polishing such that said main surface is exposed and an uppermost surface of said insulating material is substantially coplanar with said main surface;
- and
- etching said main surface by wet etching or plasma etching subsequent to chemical-mechanical polishing.
Dependencies are inferred from the claim text.