Method for a chemical vapor deposition of copper on an ion prepared conductive surface

A method of enhancing the interface conductivity of copper (Cu) applied to selected integrated circuit (IC) surfaces, the selected Cu-receiving surfaces being predominately conductive surfaces applied to selected regions of the IC, the method comprising the steps of:

• a) exposing each selected Cu-receiving surface to a low energy source of ions from an inert gas;
• b) removing contaminants from each Cu-receiving surface in response to the ion exposure in step a);
• c) exposing each Cu-receiving surface to a reactive oxygen species;
• d) oxidizing a thin layer of each Cu-receiving surface in response to the oxygen exposure in step c);
• e) stopping the exposure of each Cu-receiving surface in step c) before the oxide layer formed in step c) exceeds approximately 30 .ANG., whereby the Cu-receiving surface in cleaned in step b) to improve electrical conductivity to the deposited Cu, and the Cu-receiving surface is oxidized in step d) to improve the adhesion to the deposited Cu;
• and
• f) applying CVD Cu on each Cu-receiving surface exposed in step a), whereby the ion exposure in step a) promotes electrical conductivity between the deposited Cu and the Cu-receiving surface.

In an integrated circuit interlevel dielectric having a first surface including a conductive connection area with a connection area surface, a second surface overlying the first surface, and a via, having vertical walls between the second surface and the first surface connection area surface, a method of enhancing conductivity between a via interconnect, formed from the chemical vapor deposition (CVD) of copper, and the first surface connection area, the method comprising the steps of:

• a) depositing diffusion barrier material in the via to form a diffusion barrier surface adjoining the walls of the via and overlying the first surface connection area revealed by the via;
• b) etching the diffusion barrier surface overlying the first surface connection area, to reveal the first surface connection area surface;
• b.sub.1) exposing the diffusion barrier surface adjoining the walls of the via to a reactive oxygen species to form a thin layer of oxygen-contained barrier material over the diffusion barrier surface, whereby the subsequently deposited Cu stud better adheres to the via walls:
• c) exposing the first surface connection area surface, revealed in step b), to a low energy anisotropic source of ions from an inert gas to clean contaminants from the first surface connection area, whereby the exposure of the conduction area to ions improves the electrical conductivity of the surface to subsequently deposited Cu;
• and
• d) applying CVD Cu in the via to form a highly conductive interconnect between the first surface connection area and the second surface.

In an integrated circuit interlevel dielectric having a first surface including a semiconductor connection area with a connection area surface, a second surface overlying the first surface, and a via, having vertical walls between the second surface and the connection area surface, a method of enhancing the conductivity between a via interconnect, formed from the chemical vapor deposition (CVD) of copper, to the first surface connection area, the method comprising the steps of:

• a) depositing diffusion barrier material in the via to form a diffusion barrier surface adjoining the walls of the via and overlying the first surface connection area revealed by the via;
• b) exposing the diffusion barrier surface in the via to a source of ions from an inert gas and oxygen;
• b.sub.1) cleaning contaminants from the diffusion barrier surface in response to the inert gas ion exposure in step b), whereby the electrical conductivity between the ion-exposed diffusion barrier surface and a subsequently deposited Cu stud is improved;
• b.sub.2) simultaneously with Step b.sub.1), forming a thin layer of oxide on the diffusion barrier surface with the ions of oxygen;
• and
• b.sub.3) stopping the exposure of the diffusion barrier surface in step a) before an oxide layer is formed in step b.sub.2) that exceeds approximately 30 .ANG.;
• and
• c) applying CVD Cu in the via so that the copper stud adheres to the diffusion barrier, electrically interfacing the first surface connection area to the second surface.

A method of enhancing the interface conductivity of a metal selected from the group consisting of the metals Al, W, and Ti, applied to selected integrated circuit (IC) surfaces, the selected metal-receiving surfaces being predominately conductive surfaces applied to selected regions of the IC, the method comprising the steps of:

• a) exposing each selected metal-receiving surface to a low energy source of ions of an inert gas and oxygen;
• b) removing contaminants from each metal-receiving surface in response to the inert gas ion exposure in step a);
• b.sub.1) simultaneously with Step b), forming a thin layer of oxide on each metal-receiving surface with the ions of oxygen;
• b.sub.2) stopping the exposure of the metal-receiving surface in step a) before an oxide layer is formed in step b.sub.1) that exceeds approximately 30 .ANG., whereby ions of the inert gas are used to clean the metal-receiving surface to improve electrical conductivity, and ions of the oxygen gas are used to form a thin oxide layer on the metal-receiving surface which improves adhesion of the metal-receiving surface to metal;
• and
• c) applying CVD metal on each metal-receiving surface exposed in step a), whereby the ion exposure in step a) promotes electrical conductivity between the deposited metal and the metal-receiving surface.