Ceramic composition with low dielectric constant and method of making same
AssigneeMotorola, Inc.
InventorsJoyce K. Yamamoto, Rong-Fong Huang
Life of this patent
Estimating the term…
Abstract
Multiphase ceramic materials for use in electronic applications such as patch antennas and multilayered ceramic devices may be fabricated by providing a novel combination of a glassy precursor material with operable amounts of a high purity cordierite material. The combined materials are sintered at appropriate temperatures, so that a non-glassy celsian type phase is formed. The materials of the instant invention, fabricated according to the method disclosed herein, demonstrate low dielectric constant (K) and low electrical loss (high Q) characteristics.
Claims22
A method of fabricating a multiphase ceramic body, wherein at least one phase is a celsian type phase, said ceramic body characterized by a dielectric constant less than about 6.0 and a Q in excess of about 900, said method comprising the steps of:
- providing a glassy precursor material comprising about 40-60 wt. % BaO.sub.2, about 25-45 wt. % SiO.sub.2, about 5-25 wt. % BO.sub.2 and about 0-10 wt. % of at least one of ZrO.sub.2, ZnO.sub.2, Al.sub.2 O.sub.3, and Ca.sub.2 O.sub.3 ;
- mixing said glassy precursor material with operative amounts of a high purity cordierite material;
- and
- heating said glassy precursor material and said high purity cordierite material at temperatures in excess of about 1100.degree. C.
A substantially self-limiting method for forming a multiphase ceramic body having at least one celsian type phase, comprising the steps of reacting operative amounts of a glassy precursor material containing a barium silicate material with a cordierite material containing an aluminosilicate material so that the barium silicate material reacts with the aluminosilicate material to form the at least one celsian type phase.
A multiphase ceramic composition comprising:
- about 65-75 volume % of a glassy precursor material comprising about 40-60 wt. % BaO.sub.2, about 25-45 wt. % SiO.sub.2, about 5-25 wt. % BO.sub.2 and about 0-10 wt. % of at least one of ZrO.sub.2, ZnO.sub.2, Al.sub.2 O.sub.3, and Ca.sub.2 O.sub.3 ;
- and
- about 25-35 volume % of a high purity cordierite material.
A method of forming a multiphase ceramic composition, comprising the steps of:
- weighing out the proper concentrations and ratios of a glassy precursor material containing a barium silicate material and a high purity cordierite material and subsequently placing both of the materials in a jar;
- adding operative amounts of a dispersant;
- forming a slurry by adding water and milling media to the jar and closing and shaking until the slurry is approximately 25% of the total jar volume;
- placing the jar on a vibratory mill and milling for approximately 6-8 hours;
- rinsing the jar thoroughly with deionized water;
- straining the slurry into a drying tray;
- covering the drying tray with perforated foil and placing the drying tray in a 100.degree. C. drying oven to evaporate the water;
- grinding the dry powder using a mortar and pestle to break up agglomerates;
- adding organic binders and lubricants to the powder to form a powder/binder mixture;
- granulating the powder/binder mixture through a mesh sieve;
- placing the powder/binder mixture in a drying tray and drying in a 60.degree. C. oven for approximately 30 minutes to evaporate any residual moisture;
- and
- storing the powder in an air-tight container after the powder has been cooled to room temperature.