Abstract
A method for patterning a polysilicon layer includes creating a TiN layer above an amorphous silicon (a-Si) layer forming a TiN/a-Si stack. The TiN/a-Si stack is formed above the polysilicon layer. The TiN layer serves as an ARC to reduce overexposure of the photoresist used to pattern the polysilicon layer, while the a-Si layer prevents contamination of the layer below the polysilicon layer.
Claims4
A method for patterning a polysilicon layer using a photoresist layer above said polysilicon layer, said method comprising the steps of:
- providing a layer of amorphous silicon on the surface of said polysilicon layer;
- providing a layer of antireflective material over said layer of amorphous silicon;
- and
- providing said photoresist layer on said layer of antireflective material,
- wherein said step of providing said layer of antireflective material comprises the step of providing a titanium nitride layer.
A method for patterning a polysilicon layer using a photoresist layer above said polysilicon layer, said method comprising the steps of:
- providing a layer of amorphous silicon, said layer of amorphous silicon being at least 200 .ANG. thick, on the surface of said polysilicon layer;
- providing a layer of antireflective material over said layer of amorphous silicon;
- and
- providing said photoresist layer on said layer of antireflective material,
- wherein said layer of amorphous silicon bars diffusion of particles from said layer of antireflective material so that substantially no particles from said layer of antireflective material contact said polysilicon layer.
A method for increasing uniformity of photoresist exposure, said method comprising the steps of:
- providing a polysilicon layer on a semiconductor substrate;
- providing a temporary protective layer on said polysilicon layer;
- providing an antireflective layer on said temporary protective layer, wherein said antireflective layer reflects less light than said temporary protective layer;
- providing a photoresist layer on said antireflective layer;
- exposing and developing said photoresist layer to uncover a portion of said antireflective layer;
- and
- removing said portion of said antireflective layer and a portion of said temporary protective layer underneath said portion of said antireflective layer,
- wherein the step of providing said temporary protective layer comprises the step of providing a layer of amorphous silicon, said layer being at least 200 .ANG. thick.