Method for preparing phase shift mask blank, and phase mask
AssigneeHoya Corporation
InventorMasaru Mitsui
Life of this patent
Estimating the term…
Abstract
A light semitransmittable film of a half tone type phase shift mask blank is formed from a thin film comprising a material including oxygen, nitrogen, silicon and a metal as main constitutional components. In this case, the above-mentioned thin film is formed on a transparent substrate by a reactive sputtering process using a mixed target of molybdenum and silicon. At this time, a mixed gas of an inert gas and nitrous oxide is allowed to flow as an atmosphere gas, and the flow rate of the nitrous oxide gas is controlled within the range of 25 sccm or less to adjust the flow rate, whereby transmittance and film thickness can be controlled.
Claims22
A method for preparing a phase shift mask blank comprising the step of forming, on a transparent substrate, a light semitransmittable film, through which a light having such an intensity as not to substantially contribute to exposure can pass, from a material, comprising oxygen, nitrogen, silicon and a metal as main constitutional components, in a film formation chamber by a reactive sputtering process using a mixed target of a metal and silicon, wherein
- a mixed gas of an inert gas and nitrous oxide is allowed to flow through the film formation chamber,
- and the flow rate of nitrous oxide in the mixed gas is controlled to such a flow rate that the light transmittance, to an exposure light, of the film comprising the material including oxygen, nitrogen, silicon and the material as the main constitutional components is within a specific range.
A phase shift mask made using a phase shift mask blank prepared by forming, on a transparent substrate, a light semitransmittable film, through which a light having such an intensity as not to substantially contribute to exposure can pass, from a material, comprising oxygen, nitrogen, silicon and a metal as main constitutional components, in a film formation chamber by a reactive sputtering process using a mixed target of a metal and silicon, said phase shift mask being obtainable by
- allowing a mixed gas of an inert gas and nitrous oxide to flow through the film formation chamber, and then controlling the flow rate of nitrous oxide in the mixed gas so that the light transmittance to the exposure light of the film, comprising the material including oxygen, nitrogen, silicon and the metal as the main constitutional components, may be within a desired range, thereby preparing the phase shift mask blank,
- and then subjecting the light semitransmittable film of the thus prepared phase shift mask blank to a patterning treatment to form a pattern comprising a light semitransmittable portion and, by removing a part of the light semitransmittable film, a light transmittable portion through which a light having such an intensity as to substantially contribute to the exposure can pass.
A method for preparing a phase shift mask comprising the steps of:
- forming a phase shift mask blank by:
- forming a light semitransmittable film on a transparent substrate in a film formation chamber by a reactive sputtering process using a mixed target of a metal and silicon, said film being formed from a material comprising oxygen, nitrogen and silicon as main constitutional component and said film being one through which a light having such an intensity as not to substantially contribute to exposure can pass;
- allowing a mixed gas, including an inert gas and nitrous oxide to flow through the film formation chamber, and then controlling the flow rate of nitrous oxide in the mixed gas so that the light transmittance of the film to an exposure light is within a desired range, and;
- then subjecting the film of the phase shift mask blank to a patterning treatment to form a pattern comprising a light semitransmittable portion and, by removing a part of the semitransmittable portion, a light transmittable portion through which a light having such an intensity as to substantially contribute to exposure can pass.