Thermoplastic composition comprising chemically modified carbon black and their applications
AssigneeColumbian Chemicals Company
InventorsGeorge Alfred Joyce, Edward Lester Little
Life of this patent
Estimating the term…
Abstract
What is disclosed is an improved thermoplastic composition for use in wire and cable manufacturing processes, which features the use of from about 15 to 45 percentage by weight of a modified furnace carbon black having a specific surface area of from about 35 to 250 m.sup.2 /g, preferably 35 to 60 m.sup.2 /g, as measured by the nitrogen adsorption surface area method. The modified carbon black is prepared by combining the carbon black with a specified amount of amine, under certain conditions, and heating the reactive mixture for an extended period.
Claims11
An improved thermoplastic composition with improved resistance to elimination-type thermodegradation and thus, improved surface smoothness, resulting from a mixture comprising:
- (a) about 100 parts by weight of at least one thermoplastic selected from the group consisting of poly (ethylene-vinyl acetate);
- poly (ethylene-ethyl acrylate);
- poly (ethylene-butyl acrylate);
- poly (ethylene-methyl acrylate);
- poly (propylene-ethyl acrylate);
- and poly (vinyl chloride);
- and
- (b) from about 18 to about 82 pph polymer of a heated reaction product of a furnace carbon black and an amine wherein
- (1) the carbon black has a specific surface area from about 35 to about 60 m.sup.2 /g, ASTM D4820, and
- (2) the amine is selected from the group consisting of (a) aliphatic amines selected from the group consisting of butylamine, hexylamine, and decylamine, and (b) aromatic compounds having (1) the functional group--(CH.sub.2).sub.n NH.sub.2 attached to the aromatic ring (n is equal to 0 to about 10, or (2) both the functional group --NH.sub.2 and one or more of the following attached to the aromatic ring:
- --SH, --Cl, --NH.sub.2, or --COOH, and wherein said amine constitutes from about 0.1% to about 10.0% by weight of carbon black of the reaction product and further wherein said heated reaction product of carbon black and amine having been heated to a temperature of about 20.degree. C. over the boiling point of the amine for a period of about 0.1 to 6.0 hours.
A process for reducing elimination-type thermodegradation of a thermoplastic, and thus for reducing the surface roughness of an extruded thermoplastic, wherein the thermoplastic is selected from the group consisting of poly (ethylene-vinyl acetate);
- poly (ethylene-ethyl acrylate);
- poly (ethylene-butyl acrylate);
- poly (ethylene-methyl acrylate);
- poly (propylene-ethyl acrylate);
- and poly (vinyl chloride), and, said process comprising incorporating into the virgin thermoplastic, prior to extrusion, between from about 18 to about 82 pph polymer of a heat-treated reaction product of a furnace carbon black and an amine wherein
- (1) the carbon black has a specific surface area of from about 35 to about 60 m.sup.2 /g, ASTM D4820, and wherein
- (2) the amine is selected from the group consisting of (a) aliphatic amines selected from the group consisting of butylamine, hexylamine, and decylamine, and (b) aromatic compounds having (1) the functional group --(CH.sub.2).sub.n NH.sub.2 attached to the aromatic ring (n is equal to 0 to about 10, or (2) both the functional group --NH.sub.2 and one or more of the following attached to the aromatic ring:
- --SH, --Cl, --NH.sub.2, or --COOH, and wherein said amine constitutes from about 0.1% to about 10.0% by weight of carbon black of the reaction product, and further wherein the reaction product of furnace carbon black and amine is prepared by mixing into carbon black with the amine and heating the mixture to about the boiling point of the amine for a time sufficient to effect reaction between the amine and the carbon black.