Manufacturing method of an active material suitable for non-sintered nickel electrodes for use in alkaline storage cells

Abstract

In a method of manufacturing a nickel active material, nickel hydroxide particles coated with cobalt hydroxide are put on the mesh disk 4 of the fluidized granulator 1. Then, hot air is continuously supplied from outside through the hot air inlet 5, while air inside the fluidized granulator 5 is continuously emitted through the air outlet 8. At the same time, the nickel hydroxide particles are stirred with the stirring fan 3 and further dispersed by a hot air current. In this condition, an alkali aqueous solution is sprayed on the nickel hydroxide particles through the spray nozzle 7 by the pump 9. After the spray, the nickel hydroxide particles are further stirred in hot air so as to complete an alkali heat treatment.