US 5,702,653 AGranted

Thick-film circuit element

AssigneeSpectrol Electronics Corporation

InventorRichard E. Riley

Life of this patent

Estimating the term…

Loading patent…

Abstract

A thick-film switch element includes a high-temperature glass frit fused to a non-conductive substrate. A cermet layer having a low-temperature glass matrix is fired in a conventional furnace to sink into the glass frit layer such that the resulting thickness of the switch element layer is approximately equal to the original thickness of the glass frit layer. The wet print thickness of the cermet layer is controlled upon application of the cermet to the glass frit. The glass frit and cermet are fired at a controlled temperature and duration to achieve a fired print thickness of the cermet above the surface of the glass frit having a pre-determined value. In one embodiment, the non-conductive substrate is a metal, such as stainless steel.

Claims1

Dependent claims

A process for producing a thick-film circuit element comprising the steps of:

applying a high-temperature glass frit layer to a surface of a ceramic substrate;
applying an electrically conductive cermet layer having a low-temperature glass matrix to the surface of the glass frit layer in a circuit element pattern;
measuring a cermet layer thickness above the surface of the glass frit layer;
adjusting the cermet layer thickness until the cermet layer thickness is substantially equal to a first predetermined thickness;
firing the cermet and the glass frit layers at a temperature sufficient to cause the cermet layer to sink into the glass frit layer;
controlling the temperature and duration at which the cermet and glass frit layers are fired to control the amount that the cermet layer sinks into the glass frit layer to a second predetermined thickness above the surface of the glass frit layer;
wherein a laser profilometer is used to measure the cermet layer thickness.

4 more elements

Dependencies are inferred from the claim text.