Method of making water based paint and formed glazing with paint thereon
AssigneeFord Motor Company
InventorPremakaran Tucker Boaz
Life of this patent
Estimating the term…
Abstract
The invention is directed to a method of making a water-based paint composition comprising sodium silicate, water, water-soluble base, metal oxide pigment, soda-lime-silica glass particles and at least one of a low-melting glass frit or zinc oxide. Preferably, it comprises only the low-melting glass frit and further preferably comprises surfactants and aluminum hydroxide. In another aspect, it is also directed to a method of making a formed glazing having a cured coating of the paint composition thereon.
Claims16
A method of preparing a water-based paint composition, which has excellent adhesion to glass, which method comprises the steps of:
- (a) adding together components comprising:
- (i) water-soluble sodium silicate forming 20 to 45 weight percent of said composition,
- (ii) water forming 5 to 20 weight percent of said composition;
- (iii) water-soluble base in an amount sufficient to provide said composition with a pH of at least 10.5;
- and
- (iv) finely divided metal oxide powder selected from the group consisting of oxides of copper, iron, nickel, cobalt and mixtures thereof forming 20 to 45 weight percent of said composition and having in the prepared paint composition a particle size less than 7 microns;
- thus forming a first part of the paint composition;
- (b) adding into said first part of the paint composition, prior to using the paint composition:
- (v) particles of soda-lime-silica glass forming 10 to 55 weight percent of the composition and having a diameter in the prepared paint composition, on average, less than 20 microns and having a melting point of at least about 1700.degree. F.;
- and at least one material selected from the group consisting of:
- (vi) low-melting glass frit powder melting below 1300.degree. F. forming 0 to 10 weight percent of said composition and having a particle size in the prepared paint composition, on average, less than 10 microns;
- and
- (vii) zinc oxide forming 0 to 10 weight percent of said composition;
- and
- (c) ball milling all of said components together to form said paint composition.
A method for preparing a formed glass sheet for automotive or architectural use having a cured water-based paint thereon, which method comprises the steps of:
- applying to at least a portion of a surface of a glass sheet a water-based paint composition comprising:
- (i) water-soluble sodium silicate forming 20 to 45 weight percent of said composition,
- (ii) water forming 5 to 25 weight percent water;
- (iii) water-soluble base in an amount sufficient to provide said composition with a pH of at least 10.5;
- (iv) finely divided metal oxide powder selected from the group consisting of oxides of copper, iron, nickel, cobalt and mixtures thereof forming 20 to 45 weight percent of said composition and having a particle diameter less than 7 microns;
- (v) particles of soda-lime-silica glass forming 10 to 55 weight percent of the composition and having a diameter, on average, less than 20 microns and having a melting point of at least about 1700.degree. F.;
- and at least one material selected from the group consisting of:
- (vi) low-melting glass frit powder, having a melting point below 1300.degree. F., forming 0 to 10 weight percent of said composition and having a particle size, on average, less than 10 microns;
- and
- (vii) zinc oxide forming 0 to 10 weight percent of said composition, thus forming a painted glass sheet;
- heating the painted glass sheet by means of microwave or Infra Red radiation to a temperature below the softening point of said glass sheet, said temperature being sufficient to drive off the water present in said paint composition and cure said paint composition, thus providing an adherent coating on said glass sheet;
- cooling said painted glass sheet;
- and
- heating said painted glass sheet to a temperature sufficient to form the glass sheet into a desired shape.
Dependencies are inferred from the claim text.