Process for applying a coating to a magnesium alloy product
AssigneeSundstrand Corporation
InventorLeonard S. Joesten
Life of this patent
Estimating the term…
Abstract
This invention relates to a non-electrolytic process for applying a paint adherent and corrosion resistant coating of magnesium phosphate and magnesium fluoride to a product formed from a magnesium alloy. The process includes immersing the magnesium alloy product in a solution having phosphate and fluoride ions. The process may further include controlling a pH level of the solution, providing the solution in which the magnesium alloy product is immersed with a concentration by weight of sodium bifluoride, and controlling the solution at a certain temperature, while the magnesium alloy product is immersed for a determined period of time.
Claims3
A non-electrolytic process for applying a paint adherent and corrosion resistant coating of at least magnesium fluoride to a product formed from a magnesium alloy, comprising the steps of:
- degreasing the magnesium alloy product in an aqueous-based degreasing solution;
- cleaning the magnesium alloy product in a highly alkaline aqueous-based cleaning solution;
- deoxidizing the magnesium alloy product in a deoxidizing solution;
- and
- immersing the magnesium alloy product in a solution having phosphate and fluoride ions wherein a pH level of the solution is controlled in an approximate range of 5 to 7, the solution being provided with a concentration by weight of sodium bifluoride at a concentration of about 0.3-0.5%, and being maintained at a temperature of approximately 130 degrees Fahrenheit while immersing the magnesium alloy product for a period of approximately thirty minutes.
A non-electrolytic process for applying a paint adherent and corrosion resistant coating of at least magnesium phosphate and magnesium fluoride to a product formed from a magnesium alloy, comprising the steps of:
- degreasing the magnesium alloy product in an aqueous-based degreasing solution;
- cleaning the magnesium alloy product in a highly alkaline aqueous-based cleaning solution;
- deoxidizing the magnesium alloy product in a deoxidizing solution;
- and
- immersing the magnesium alloy product in a solution having phosphate and fluoride ions wherein a pH level of the solution is controlled in an approximate range of 5 to 7, the solution being provided with a concentration by weight of sodium bifluoride at a concentration of about 0.3-0.5% and being maintained at a temperature of approximately 130 degrees Fahrenheit while immersing the magnesium alloy product for a period of approximately thirty minutes.
A non-electrolytic process for applying a paint adherent and corrosion resistant coating of at least magnesium phosphate to a product formed from a magnesium alloy, comprising the steps of:
- degreasing the magnesium alloy product in an aqueous-based degreasing solution;
- cleaning the magnesium alloy product in a highly alkaline aqueous-based cleaning solution;
- deoxidizing the magnesium alloy product in a deoxidizing solution;
- and
- immersing the magnesium alloy product in a solution having phosphate and fluoride ions wherein a pH level of the solution is controlled in an approximate range of 5 to 7, the solution being provided with a concentration by weight of sodium bifluoride at a concentration of about 0.3-0.5% and being maintained at a temperature of approximately 130 degrees Fahrenheit while immersing the magnesium alloy product for a period of approximately thirty minutes.