Plasma etch process and TiSi.sub.x layers made using the process
AssigneeVarian Associates, Inc.
InventorsMichelangelo Delfino, Mary E. Day, Wilman Tsai
Life of this patent
Estimating the term…
Abstract
A method for making an improved metal silicide layer on a silicon substrate by plasma bombardment of the substrate with Ne ions to remove the native oxide without damage or significant implantation of Ne atoms into said silicon, depositing a metal layer over the Ne etched surface and then rapidly thermally causing the metal layer to react with the underlying silicon.
Claims8
A method for making an improved metal silicide layer on a silicon substrate having a native oxide layer thereon comprising,
- installing said silicon substrate in a vacuum chamber;
- exciting in said vacuum chamber a downstream neon microwave plasma employing an electron cyclotron resonance apparatus and flowing said plasma towards said substrate in said plasma chamber and bombarding said substrate with neon ions from said plasma;
- stopping said bombardment when essentially all native oxide on said substrate is volatized;
- depositing a metal layer on said substrate;
- annealing said metal layer at a temperature high enough to cause said metal and said silicon underlying said metal to chemically react to form a metal silicide.
A method for making improved via interconnects on a partially processed semiconductor integrated circuit wafer which has been processed up to first level metallization comprising;
- (a) inserting said wafer into a vacuum chamber;
- (b) exciting in said vacuum chamber an ECR neon plasma and bombarding said wafer with low energy neon ions on the order of 50-250 volts from said plasma to volatilize native oxide without embedding heavy noble gas ions in said wafer;
- (c) stopping said bombardment when essentially all native oxide on said substrate is volatized;
- (d) sputter depositing a titanium layer on said wafer, said titanium layer to become the metal reaction component of a silicide first level metallization;
- (e) annealing said titanium layer at a temperature high enough to react said titanium and the neon plasma cleaned silicon underlying and in direct contact with said titanium, said annealing carried out in a N.sub.2 or NH.sub.3 environment so that a TiN or TiO.sub.x N.sub.y layer forms above a TiSi.sub.2 layer;
- (f) creating first metallization mask for patterning said first layer metal interconnects by applying resist, photographically exposing said resist and developing said resist;
- (h) dry etching through said first metallization mask to create first interconnects;
- (i) depositing on said annealed layer a field oxide for isolating said metallization;
- (j) planarizing said field oxide;
- (k) creating a via pattern mask on top of said field oxide by applying resist, photographically exposing said resist and developing said resist;
- (l) dry etching said field oxide through said via pattern mask to create via holes, said etching proceeds through said field oxide and stops in said TiN or TiO.sub.x N.sub.y layer;
- (m) filling said via holes with aluminum by sputtering aluminum into said via holes without removing said Ti N or TiO.sub.x N.sub.y layer atop said TiSi.sub.2 whereby said TiN or TiO.sub.x N.sub.y comprises an Al diffusion barrier.
Dependencies are inferred from the claim text.