US 5,597,756 A · Process for fabricating a cup-shaped DRAM capacitor using a multi-layer partly-sacrificial stack

Abstract

This invention is a process for fabricating a dynamic random access memory (DRAM) having a stacked capacitor with hemispherical-grain (HSG) polysilicon asperities on an amorphous silicon storage-node plate. The process enables the selective formation of HSG polysilicon asperities on the storage-node plates and a subsequent deposition of a high-quality silicon nitride cell dielectric layer on the asperity-covered storage-node plates. The process is preferably initiated following field oxide formation, wordline formation, access transistor source/drain region formation, deposition of a planarizing dielectric layer, formation of bitline contact and storage-node contact openings in the planarizing layer, and formation of conductive plugs in both types of contact openings. The process is implemented by sequentially depositing a first tetraethylorthosilicate (TEOS) oxide layer, a first silicon nitride layer, a second TEOS oxide layer, a second silicon nitride layer, and a boro-phospho-silicate glass (BPSG) layer to form a multi-layer partly-sacrificial stack. Depressions are etched in the partly-sacrificial stack and amorphous silicon cup-shaped storage-node plates are formed in the depressions. Following removal of the BPSG layer and the second silicon nitride layer, HSG polysilicon asperities are formed on the plates. The second TEOS oxide layer is then removed, exposing the first silicon nitride layer. A silicon nitride cell dielectric layer is then deposited over the surface of the array.

Claims29

Dependent claims

A method of forming a dynamic random access memory cell capacitor, said method comprising the following steps:

(a) providing a silicon substrate having a storage-node junction on an upper surface thereof;
(b) depositing alternating layers of silicon dioxide and silicon nitride superjacent the substrate;
(c) etching a hole through the alternating layers directly above the storage-node junction;
(d) forming a storage-node plate from an amorphous silicon layer which is in electrical communication with the storage-node junction through the hole, and which is in contact with at least an edge of each of said alternating layers;
(e) forming HSG polysilicon asperities on only the storage-node plate while one of said silicon dioxide layers is exposed;
(f) removing said one of said silicon dioxide layers to expose an underlying silicon nitride layer;
(g) forming a cell dielectric layer on the asperity-covered storage-node plate;
and
(h) depositing a cell plate layer on top of the cell dielectric layer.

6 more elements

A method of forming a dynamic random access memory cell capacitor comprising the following steps:

(a) providing a base dielectric layer through which a vertically oriented polysilicon plug makes contact to a subjacent storage-node junction of a memory cell access device;
(b) depositing a first silicon nitride layer superjacent the base dielectric layer;
(c) depositing a silicon dioxide layer on top of the first silicon nitride layer;
(d) depositing a second silicon nitride layer on top of the silicon dioxide layer;
(e) depositing a mold layer on top of the second silicon nitride layer;
(f) forming a depression in the mold layer and all intervening layers between the mold layer and the base dielectric layer, such that said depression exposes at least an upper surface of the polysilicon plug;
(g) depositing an amorphous silicon layer which lines the depression, which is in direct contact with said polysilicon plug, and which covers an upper surface of the mold layer;
(h) removing a portion of the amorphous silicon layer which covers the upper surface of the mold layer, thus forming a singulated storage-node plate;
(i) removing the mold layer so as to expose the second silicon nitride layer;
(j) removing the second silicon nitride layer to expose the silicon dioxide layer;
(k) forming HSG polysilicon asperities on only the storage-node plate;
(l) removing the silicon dioxide layer so as to expose the first silicon nitride layer;
(m) depositing a cell dielectric layer on the asperity-covered storage-node plate;
and
(n) depositing a cell plate layer on top of the cell dielectric layer.

12 more elements

Dependencies are inferred from the claim text.

Process for fabricating a cup-shaped DRAM capacitor using a multi-layer partly-sacrificial stack

Life of this patent

Process for fabricating a cup-shaped DRAM capacitor using a multi-layer partly-sacrificial stack

Life of this patent

Abstract

Claims29