Process for forming a sparingly soluble chromate coating on zinciferous metal coated steel
AssigneeHenkel Corporation
InventorsTakao Ogino, Shinji Nomura
Life of this patent
Estimating the term…
Abstract
A highly corrosion-resistant, highly alkali-resistant, and very paintable chromate film on the surface of a steel substrate coated with Zn-containing metal is formed by coating the substrate with an aqueous chromate bath and drying into place, preferably at a substrate temperature of 60.degree. to 200.degree. C., without a water rinse. The bath contains Cr.sup.6+, Cr.sup.3+, phosphate ions, water-soluble glycol ether (WSGE) and/or poly{vinyl alcohol} (PVA), and optionally silica sol, in amounts giving ratios of Cr.sup.3+ /Cr.sup.6+ =0.25 to 4.0, PO.sub.4 /total Cr=0.1 to 2.5, and (WSGE+PVA)/Cr.sup.6+ =0.1 to 0.5 in the bath.
Claims14
A process for the formation of a solid sparingly soluble chromate coating on the outer surface of a steel substrate coated with zinc-containing metal, said process comprising steps
- (I) covering the outer surface of the substrate with a layer of an aqueous liquid treatment composition consisting essentially of:
- (A) an aqueous mixture, said aqueous mixture containing
- (I.A) 1.0 to 40.0 g/L of hexavalent chromium
- (I.B) 1.0 to 40.0 g/L of trivalent chromium ions;
- and
- (I.C) 0.4 to 100 g/L of phosphate ions,
- the concentration of hexavalent chromium ions, and trivalent chromium ions and phosphate ions being selected so as to result in a (trivalent chromium ions)/(hexavalent chromium ions) ratio of 0.25 to 4.0 in said aqueous mixture and a (phosphate ions/total chromium ions) ratio of 0.1 to 2.5 in said aqueous mixture, admixed with
- (B) a component (I.D) selected from the group consisting of poly{vinyl alcohols} ("PVA") and water-soluble glycol ethers ("WSGE") having an average molecular weight of 62 to 20,000 in an amount such as to result in a (WSGE+PVA)/(hexa-valent chromium ions) weight ratio of 0.1 to 0.5 in said aqueous liquid treatment composition,
- wherein the thickness of the layer of the aqueous liquid treatment composition covering the outer surface of the substrate is such as to contain from 5 to 200 mg/m.sup.2 of chromium, and
- (II) drying into place on the treated surface of the substrate the liquid layer formed on the treated surface in step (I), without any intermediate rinsing, whereby the solid sparingly soluble chromate coating is formed and incorporates the nonvolatile contents of the liquid layer formed on the treated surface in step (I).
An aqueous liquid composition of matter suitable for treating the surface of a zinc-containing metal coated steel substrate to form a solid sparingly soluble chromate containing protective coating thereon after drying into place, wherein said aqueous liquid composition is an admixture of (A) an aqueous solution of hexachromium ions, trivalent chromium ions, and phosphate ions and (B) an amount of a component selected from the group consisting of poly{vinyl alcohols} ("PVA") and water soluble glycol ethers ("WSGE"),
- wherein said aqueous solution consists essentially of water and:
- 1.0 to 40.0 g/L of hexavalent chromium ions;
- 1.0 to 40.0 g/L o trivalent chromium ions;
- and
- 0.4 to 100 g/L of phosphate ions,
- wherein component (B) is selected from the group consisting of poly{vinyl alcohols} ("PVA") and water-soluble glycol ethers ("WSGE") having an average molecular weight of 62 to 20,000, in an amount of component (B) such as to result in a (WSGE+PVA)/(hexavalent chromium ions) weight ratio of 0.1 to 0.5 in said aqueous liquid composition, and
- wherein the concentrations of hexavalent chromium ions, trivalent chromium ions and phosphate ions in said aqueous solution result in a (trivalent chromium ions)/(hexavalent chromium ions) ratio of 0.25 to 4.0 in said aqueous solution and a (phosphate ions)/(total chromium ions) ratio of 0.1 to 2.5 in said aqueous solution.
Dependencies are inferred from the claim text.