Production of spray deposits
AssigneeOsprey Metals Limited
InventorsJames B. Forrest, Charles R. Pratt, Jeffrey S. Coombs
Life of this patent
Estimating the term…
Abstract
A method and apparatus for the production of a deposit such as a bar (1) is provided. The deposit has a longitudinal outer surface (2) and a front face deposition surface (3). The spray deposition comprises atomized droplets produced by outer and inner sprays (4 and 5). The outer and inner sprays (4 and 5) are both directed such that, during deposition, a substantial proportion of droplets from both sprays are deposited on the front face (3) of the forming deposit. The inner spray (5) has a higher gas to metal ratio than the outer spray allowing an increase of both deposition and final product yield.
Claims13
A method of producing an elongate spray deposit such as a round bar or billet by spray deposition comprising the steps of:
- gas atomizing a first stream of metal or metal alloy to form a first spray of atomized droplets;
- gas atomizing a second stream of metal or metal alloy to form a second spray of atomized droplets;
- depositing the atomized droplets of the first and second sprays to form a coherent elongate deposit having a longitudinal outer surface and a front face;
- positioning the first and second sprays to deposit a substantial proportion of the droplets from both sprays on the front face of the forming deposit;
- the first and second sprays being positioned as inner and outer sprays with respect to a longitudinal axis of the deposit, and the atomized droplets of the inner spray having a lower heat content than the atomized droplets of the outer spray.
A method of increasing deposition yield in the spray deposition of an elongate deposit and reducing surface porosity in a longitudinal surface of the deposit, the method comprising the steps of:
- (a) atomizing a first stream of metal or metal alloy to form a first spray of atomized droplets;
- (b) atomizing a second stream of metal or metal alloy to form a second spray of atomized droplets;
- (c) co-depositing the atomized droplets of the first and second sprays on a deposition surface defined, initially by a substrate and, thereafter, by previously deposited droplets;
- (d) rotating and withdrawing the substrate during deposition so that a substantially constant spray distance is maintained to the deposition surface and whereby a coherent elongate deposit having a longitudinal outer surface and a front face is formed;
- (e) positioning the first and second sprays such that they form, respectively, inner and outer sprays with respect to the longitudinal axis of the deposit and during deposition, the sprays overlap and a substantial proportion of droplets from both sprays are deposited on the front face of the forming deposit;
- and,
- (f) controlling the heat content of the two sprays whereby the first spray is deposited at a lower heat content than the second spray to prevent the central portion overheating and allowing an increase in deposition yield and to reduce surface porosity in the longitudinal surface of the deposit thereby increasing overall product yield.
Dependencies are inferred from the claim text.