Silicon nitride sintered body
AssigneeSumitomo Electric Industries, Ltd.
InventorsAkira Yamakawa, Koichi Sogabe
Life of this patent
Estimating the term…
Abstract
A silicon nitride sintered body comprising 3.5% by weight or less of aluminum, 3.5% by weight or less of oxygen and the balance of silicon nitride; and a silicon nitride sintered body comprising 90% by weight or more of silicon nitride, 3.5% by weight or less of aluminum, 3.5% by weight or less of oxygen and from 0.01 to 10% by weight of at least one metallic element selected from the group consisting of Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Fin, Fe, Co, Ni, Nd, and Ho. These sintered bodies have a density of 3.15 g/cm.sup.3 or more and a thermal conductivity of 40 W/mK or more.
Claims6
A silicon nitride sintered body comprising 3.5% by weight or less of aluminum, 3.5% by weight or less of oxygen and the balance of silicon nitride, said sintered body having a density of 3.15 g/cm.sup.3 or more and a thermal conductivity of 40 W/mK or more, wherein the extinction coefficient thereof for light having a wavelength of 5 .mu.m is 60 cm.sup.-1 or less, wherein the sintered body is produced by:
- molding Si.sub.3 N.sub.4 powder having an average particle diameter of 2 .mu.m or less, an oxygen content of 1.5% by weight or less, and an impurity cation and anion amount of 1.0% by weight or less;
- and
- sintering the resulting molding at 1,500.degree. to 2,200.degree. C. in a non-oxidizing gas atmosphere containing N.sub.2.
A silicon nitride sintered body comprising 90% by weight or more of silicon nitride, 3.5% by weight or less of aluminum, 3.5% by weight or less of oxygen and from 0.01 to 10% by weight of at least one metallic element selected from the group consisting of Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Mn, Fe, Co, and Ni, said sintered body having a density of 3.15 g/cm.sup.3 or more and a thermal conductivity of 40 W/mK or more, wherein the extinction coefficient thereof for light having a wavelength of 5 .mu.m is 60 cm.sup.-1 or more, wherein the sintered body is produced by:
- molding Si.sub.3 N.sub.4 powder having an average particle diameter of 2 .mu.m or less, an oxygen content of 1.5% by weight or less, and an impurity cation and anion amount of 1.0% by weight or less;
- and
- sintering the resulting molding at 1,500.degree. to 2,200.degree. C. in a non-oxidizing gas atmosphere containing N.sub.2.
A silicon nitride sintered body comprising 3.5% by weight or less of aluminum, 3.5% by weight or less of oxygen, a sintering aid, provided that said sintering aid does not form a solid solution with the silicon nitride, and the balance of silicon nitride, said sintered body having a density of 3.15 g/cm.sup.3 or more and a thermal conductivity of 40 W/mK or more, wherein the extinction coefficient thereof for light having a wavelength of 5 .mu.m is 60 cm.sup.-1 or less,
- wherein the sintered body is produced by:
- molding Si.sub.3 N.sub.4 powder having an average particle diameter of 2 .mu.m or less, an oxygen content of 1.5% by weight or less, and an impurity cation and anion amount of 1.0% by weight or less;
- and
- sintering the resulting molding at 1,500.degree. to 2,200.degree. C. in a non-oxidizing gas atmosphere containing N.sub.2.
Dependencies are inferred from the claim text.