Method of producing titanium material resistant to hydrogen absorption in aqueous hydrogen sulfide solution
AssigneeNippon Mining & Metals Co., Ltd.
InventorsKazuhiro Taki, Akio Saito
Life of this patent
Estimating the term…
Abstract
A method of producing a titanium material having enhanced resistance to hydrogen absorption in aqueous hydrogen sulfide solutions which comprises removing a layer of at least 0.5 .mu.m depth from the surface of a titanium material that has been annealed after cold rolling so that titanium nitride, titanium carbide, or titanium carbonitride formed on the surface is removed. It is preferable that the titanium material has no flaw in the depth beyond 10 .mu.m from the surface. It is desirable that the titanium material is polished so that it has a surface roughness Rmax not exceeding 3.0 .mu.m. It is also preferred that the titanium surface has an oxide film ranging in thickness from 15 to 500 nm formed thereon.
Claims8
A method of producing a titanium material having enhanced resistance to hydrogen absorption in an aqueous hydrogen sulfide solution, comprising the steps of:
- i) subjecting a titanium material to cold working with the use of a working oil, with the degree of the cold working being 10% or more of the total cold reduction, to produce a cold-worked titanium material;
- ii) heat treating the cold-worked titanium material at a temperature of from 300.degree. C. to 850.degree. C. in vacuum or in an inert gas atmosphere to produce a titanium material with a layer of at least one of titanium nitride, titanium carbide and titanium carbonitride formed on the surface thereof;
- and
- iii) removing said surface layer to a depth of at least 0.5 .mu.m so that titanium nitride, titanium carbide and titanium carbonitride formed on the titanium material surface is at least partly removed, thereby imparting enhanced resistance to hydrogen absorption in aqueous hydrogen sulfide solutions to said titanium material.
Dependencies are inferred from the claim text.