US 5,393,699 AGranted
Deposited film formation method utilizing selective deposition by use of alkyl aluminum hydride
AssigneeCanon Kabushiki Kaisha
InventorsNobuo Mikoshiba, Kazuo Tsubouchi, Kazuya Masu
Life of this patent
Estimating the term…
Abstract
By providing a deposited film formation method in which aluminum or a metal composed mainly of aluminum of good quality is selectively deposited according to the CVD method utilizing an alkyl aluminum hydride and hydrogen, and then pure aluminum or a metal composed mainly of aluminum is non-selectively deposited, it becomes possible to form an electroconductive film of good quality within fine openings or on an insulating layer.
Claims21
A deposited film formation method comprising the steps of:
- (a) arranging a substrate having an electron donative surface (A) and an electron non-donative surface (B) in a space for deposited film formation,
- (b) introducing a gas of an alkyl aluminum hydride and hydrogen gas into said space for deposited film formation,
- (c) maintaining the temperature of said electron donative surface (A) within the range of from the decomposition temperature of said alkyl aluminum hydride to 450.degree. C., thereby forming selectively an aluminum film or a metal film composed mainly of aluminum on said electron donative surface (A), and
- (d) modifying the surface of said electron non-donative surface (B), and forming an aluminum film or a metal film composed mainly of aluminum on said surface (B) and on said selectively formed aluminum film or the metal film composed mainly of aluminum employing a gas of an alkyl aluminum hydride, wherein the surface modification of step (d) is performed by forming a nucleus containing free electrons on said surface (B).
1 more element
A deposited film formation method comprising the steps of:
- (a) arranging a substrate having an electron donative surface (A) and an electron non-donative surface (B) in a space for deposited film formation,
- (b) introducing a gas of an alkyl aluminum hydride and hydrogen gas into said space for deposited film formation,
- (c) maintaining the temperature of said electron donative surface (A) within the range of from the decomposition temperature of said alkyl aluminum hydride to 450.degree. C., thereby forming selectively an aluminum film or a metal film composed mainly of aluminum on said electron donative surface (A), and
- (d) modifying the surface of said electron non-donative surface (B), and forming an aluminum film or a metal film composed mainly of aluminum on said surface (B) and on said selectively formed aluminum film or the metal film composed mainly of aluminum employing a gas of an alkyl aluminum hydride, wherein the surface modification of step (d) is performed by forming a thin film containing free electrons on said surface (B).
1 more element
A deposited film formation method comprising the steps of:
- (a) arranging a substrate having an electron donative surface (A) and an electron non-donative surface (B) in a space for deposited film formation,
- (b) introducing a gas of an alkyl aluminum hydride and hydrogen gas into said space for deposited film formation,
- (c) maintaining the temperature of said electron donative surface (A) within the range of from the decomposition temperature of said alkyl aluminum hydride to 450.degree. C., thereby forming selectively an aluminum film or a metal film composed mainly of aluminum on said electron donative surface (A), and
- (d) modifying the surface of said electron non-donative surface (B), and forming an aluminum film or a metal film composed mainly of aluminum on said surface (B) and on said selectively formed aluminum film or the metal film composed mainly of aluminum employing a gas of an alkyl aluminum hydride, wherein said surface modification is carried out by elevating the temperature of said electron non-donative surface (B) higher than the temperature during said selective deposition of aluminum film.
1 more element
A deposited film formation method comprising the steps of:
- (a) arranging a substrate having an electron donative surface (A) and an electron non-donative surface (B) in a space for deposited film formation,
- (b) introducing a gas of an alkyl aluminum hydride and hydrogen gas into said space for deposited film formation,
- (c) maintaining the temperature of said electron donative surface (A) within the range of from the decomposition temperature of said alkyl aluminum hydride to 450.degree. C., thereby forming selectively an aluminum film or a metal film composed mainly of aluminum on said electron donative surface (A), and
- (d) modifying the surface of said electron non-donative surface (B), and forming an aluminum film or a metal film composed mainly of aluminum on said surface (B) and on said selectively formed aluminum film or the metal film composed mainly of aluminum employing a gas of an alkyl aluminum hydride, wherein said surface modification includes the step of irradiating a light having greater energy than the optical forbidden gap width of the material constituting said surface (B).
1 more element
A deposited film formation method comprising the steps of:
- (a) arranging a substrate having an electron donative surface (A) and an electron non-donative surface (B) in a space for deposited film formation,
- (b) introducing a gas of an alkyl aluminum hydride and hydrogen gas into said space for deposited film formation,
- (c) maintaining the temperature of said electron donative surface (A) within the range of from the decomposition temperature of said alkyl aluminum hydride to 450.degree. C., thereby forming selectively an aluminum film or a metal film composed mainly of aluminum on said electron donative surface (A), and
- (d) modifying the surface of said electron non-donative surface (B), and forming an aluminum film or a metal film composed mainly of aluminum on said surface (B) and on said selectively formed aluminum film or the metal film composed mainly of aluminum employing a gas of an alkyl aluminum hydride, wherein said surface modification includes the step of irradiating said surface (B) with ions.
1 more element
A deposited film formation method comprising the steps of:
- (a) arranging a substrate having an electron donative surface (A) and an electron non-donative surface (B) in a space for deposited film formation,
- (b) introducing a gas of an alkyl aluminum hydride and hydrogen gas into said space for deposited film formation,
- (c) maintaining the temperature of said electron donative surface (A) within the range of from the decomposition temperature of said alkyl aluminum hydride to 450.degree. C., thereby forming selectively an aluminum film or a metal film composed mainly of aluminum on said electron donative surface (A), and
- (d) modifying the surface of said electron non-donative surface (B), and forming an aluminum film or a metal film composed mainly of aluminum on said surface (B) and on said selectively formed aluminum film or the metal film composed mainly of aluminum employing a gas of an alkyl aluminum hydride, wherein said surface modification includes the step of irradiating said surface (B) with an electron beam.
1 more element
A deposited film formation method comprising the steps of:
- (a) arranging a substrate having an electron donative surface (A) and an electron non-donative surface (B) in a space for deposited film formation,
- (b) introducing a gas of an alkyl aluminum hydride, a gas containing silicon atoms and hydrogen gas into said space for deposited film formation,
- (c) maintaining the temperature of said electron donative surface (A) within the range of the decomposition temperature of said alkyl aluminum hydride to 450.degree. C., thereby forming selectively an aluminum film or a metal film composed mainly of aluminum containing silicon on said electron donative surface (A), and
- (d) modifying the surface of said electron non-donative surface (B), and forming an aluminum film or a metal film composed mainly of aluminum on said modified surface (B) employing a gas of an alkyl aluminum hydride, wherein the surface modification of step (d) is performed by forming a nucleus containing free electrons on said surface (B).
1 more element
A deposited film formation method, comprising the steps of:
- (a) arranging a substrate having an electron donative surface (A) and an electron non-donative surface (B) in a space for deposited film formation,
- (b) introducing a gas of an alkyl aluminum hydride, a gas containing silicon atoms and hydrogen gas into said space for deposited film formation,
- (c) maintaining the temperature of said electron donative surface (A) within the range of the decomposition temperature of said alkyl aluminum hydride to 450.degree. C., thereby forming selectively an aluminum film or a metal film composed mainly of aluminum containing silicon on said electron donative surface (A), and
- (d) modifying the surface of said electron non-donative surface (B), and forming an aluminum film or a metal film composed mainly of aluminum on said modified surface (B) employing a gas of an alkyl aluminum hydride, wherein the surface modification of step (d) is performed by forming a thin film containing free electrons on said surface (B).
1 more element
A deposited film formation method comprising the steps of:
- (a) arranging a substrate having an electron donative surface (A) and an electron non-donative surface (B) in a space for deposited film formation,
- (b) introducing a gas of an alkyl aluminum hydride, a gas containing silicon atoms and hydrogen gas into said space for deposited film formation,
- (c) maintaining the temperature of said electron donative surface (A) within the range of the decomposition temperature of said alkyl aluminum hydride to 450.degree. C., thereby forming selectively an aluminum film or a metal film composed mainly of aluminum containing silicon on said electron donative surface (A), and
- (d) modifying the surface of said electron non-donative surface (B), and forming an aluminum film or a metal film composed mainly of aluminum on said modified surface (B) employing a gas of an alkyl aluminum hydride, wherein said surface modification is carried out by elevating the temperature of said electron non-donative surface (B) higher than the temperature during said selective deposition of aluminum film containing silicon.
1 more element
A deposited film formation method comprising the steps of:
- (a) arranging a substrate having an electron donative surface (A) and an electron non-donative surface (B) in a space for deposited film formation,
- (b) introducing a gas of an alkyl aluminum hydride, a gas containing silicon atoms and hydrogen gas into said space for deposited film formation,
- (c) maintaining the temperature of said electron donative surface (A) within the range of the decomposition temperature of said alkyl aluminum hydride to 450.degree. C., thereby forming selectively an aluminum film or a metal film composed mainly of aluminum containing silicon on said electron donative surface (A), and
- (d) modifying the surface of said electron non-donative surface (B), and forming an aluminum film or a metal film composed mainly of aluminum on said modified surface (B) employing a gas of an alkyl aluminum hydride, wherein said surface modification includes the step of irradiating a light having greater energy than the optical forbidden gap width of the material constituting said surface (B).
1 more element
A deposited film formation method comprising the steps of:
- (a) arranging a substrate having an electron donative surface (A) and an electron non-donative surface (B) in a space for deposited film formation,
- (b) introducing a gas of an alkyl aluminum hydride, a gas containing silicon atoms and hydrogen gas into said space for deposited film formation,
- (c) maintaining the temperature of said electron donative surface (A) within the range of the decomposition temperature of said alkyl aluminum hydride to 450.degree. C., thereby forming selectively an aluminum film or a metal film composed mainly of aluminum containing silicon on said electron donative surface (A), and
- (d) modifying the surface of said electron non-donative surface (B), and forming an aluminum film or a metal film composed mainly of aluminum on said modified surface (B) employing a gas of an alkyl aluminum hydride, wherein said surface modification includes the step of irradiating said surface (B) with ions.
1 more element
A deposited film formation method comprising the steps of:
- (a) arranging a substrate having an electron donative surface (A) and an electron non-donative surface (B) in a space for deposited film formation,
- (b) introducing a gas of an alkyl aluminum hydride, a gas containing silicon atoms and hydrogen gas into said space for deposited film formation,
- (c) maintaining the temperature of said electron donative surface (A) within the range of the decomposition temperature of said alkyl aluminum hydride to 450.degree. C., thereby forming selectively an aluminum film or a metal film composed mainly of aluminum containing silicon on said electron donative surface (A), and
- (d) modifying the surface of said electron non-donative surface (B), and forming an aluminum film or a metal film composed mainly of aluminum on said modified surface (B) employing a gas of an alkyl aluminum hydride, wherein said surface modification includes the step irradiating said surface (B) with an electron beam.
1 more element
A deposited film formation method comprising the steps of:
- (a) arranging a substrate having an electron donative surface (A) and an electron non-donative surface (B) in a space for deposited film formation in a deposited film formation device equipped with a plasma generation means for generating a plasma,
- (b) introducing a gas of an alkyl aluminum hydride and hydrogen gas into said space for deposited film formation,
- (c) maintaining the temperature of said electron donative surface (A) within the range of the decomposition temperature of said alkyl aluminum hydride to 450.degree. C., thereby forming selectively an aluminum film or a metal film composed mainly of aluminum on said electron donative surface (A),
- (d) modifying the surface of said electron non-donative surface (B) by generating a plasma in said device while introducing said gas of alkyl aluminum hydride and hydrogen gas, and
- (e) forming an aluminum film or a metal film composed mainly of aluminum on said selectively formed aluminum film or metal film composed mainly of aluminum and on said modified electron non-donative surface (B).
2 more elements
A deposited film formation method comprising the steps of:
- (a) arranging a substrate having an electron donative surface (A) and an electron non-donative surface (B) in a space for deposited film formation in a deposited film formation device equipped with a plasma generation means for generating a plasma,
- (b) introducing a gas of an alkyl aluminum hydride, a gas containing silicon atom and hydrogen gas into said space for deposited film formation,
- (c) maintaining the temperature of said electron donative surface (A) within the range of the decomposition temperature of said alkyl aluminum hydride to 450.degree. C., thereby forming selectively an aluminum film or metal film composed mainly of aluminum containing silicon on said electron donative surface (A),
- (d) modifying the surface of said electron non-donative surface (B) by generating a plasma in said device while introducing said gas of alkyl aluminum hydride, gas containing silicon atoms and hydrogen gas, and
- (e) forming an aluminum film or metal film composed mainly of aluminum containing silicon (i) on said selectively formed aluminum film or metal film composed mainly of aluminum containing silicon and (ii) on said modified electron non-donative surface (B).
2 more elements
Dependencies are inferred from the claim text.