Composite sliding member with impregnated mesh layer
AssigneeDaido Metal Company Ltd.
InventorsTadashi Tanaka, Hidehiko Tamura, Nobutaka Hiramatsu, Takuya Tanaka
Life of this patent
Estimating the term…
Abstract
A composite sliding member includes a metal wire mesh or expanded metal impregnated and covered with a composition of 0.1-50% by volume of one or more of PFA, FEP and EPE, and 0.1-50% by volume of at least one of oxybenzoyl polyester, polyphenylene sulfide, thermosetting resin, metal lubricant, metal oxide, composite metal oxide, metal sulfide, metal fluoride, carbon-based self lubricant, fiber material, and ceramics, with the remainder being substantially PTFE.
Claims5
A composite sliding member, comprising a base composed of a metal wire mesh or expanded metal having a void portion and surface covered and impregnated with a lubricating composition comprising 0.1-50% by volume of at least one kind of resin selected from a group (A) consisting of tetrafluoroethylene-perfluoroalkylvinylether copolymer resin, tetrafluoroethylene-hexafluoropropylene copolymer resin, and fluoroethylene-propyleneether resin, 0.1-50% by volume of at least one kind selected from a group (B) consisting of oxybenzoyl polyester, polyphenylene sulfide, thermosetting resin, metal lubricant, metal oxide, composite metal oxide, metal sulfide, metal fluoride, carbon-based self lubricant, fiber material and ceramics, and the remaining of substantially tetrafluoroethylene resin, wherein the total of the components other than the tetrafluoroethylene resin is 0.2-70% by volume.
A composite sliding member, comprising a base composed of a metal wire mesh or expanded metal mesh coated and impregnated with a lubricating composition consisting essentially of
- 2-30% by volume of a first component (A) consisting of a member selected from the group consisting of tetrafluoroethylene-perfluoroalkylvinylether copolymer resin, tetrafluoroethylene-hexafluoropropylene copolymer resin, fluoroethylene-propylene ether resin, and mixtures thereof,
- 2-30% by volume of a second component (B) selected from the group consisting of oxybenzoyl polyester, polyphenylene sulfide, thermosetting resin, metal lubricant, metal oxide, composite metal oxide, metal sulfide, metal fluoride, carbon-based self lubricant, fiber material and ceramics, and
- the remainder being tetrafluoroethylene resin, said tetrafluoroethylene resin and said component (A) being sintered together to form a mutual solution thereof.
A composite sliding member, comprising a base composed of a metal wire mesh or expanded metal mesh coated and impregnated with a lubricating composition consisting essentially of
- 2-30% by volume of a first component (A) consisting of a member selected from the group consisting of tetrafluoroethylene-perfluoroalkylvinylether copolymer resin, tetrafluoroethylene-hexafluoropropylene copolymer resin, fluoroethylene-propylene ether resin, and mixtures thereof,
- 2-30% by volume of a second component (B) selected from the group consisting of oxybenzoyl polyester, polyphenylene sulfide, thermosetting resin, metal oxide, composite metal oxide, metal sulfide, metal fluoride, carbon-based self lubricant, fiber material and ceramics, and
- the remainder being tetrafluoroethylene resin.
Dependencies are inferred from the claim text.