US 5,352,481 A · Process for forming particles having a uniform size distribution

Abstract

A process is provided for fabricating coated particles of a substantially uniform particle size. The process comprises coating small particles of well-defined crystalline phases with a polymerized gel. The process results in a ball-type sol-gel coating of the particles to provide particles which have a narrow size distribution. In many instances, crystalline particles of irregular shape have a substantially spherical shape upon coating with the sol-gel. In instances where the core is a high melting point material, such as an oxide, nitride, or carbide, the coat formulation can effect a low sintering temperature, which permits forming films of the particles at a much lower temperature than would otherwise be possible.

Claims8

Dependent claims

A process for forming particles having a substantially uniform size distribution and provided with an outer coating having a melting point of less than 900.degree. C. to enable sintering of said particles at a temperature less than 900.degree. C., comprising:

(a) providing titania powder comprising core particles of irregular shape and broad particle size distribution;
(b) coating said titania powder with a first coating consisting essentially of a silica gel by
(1) suspending said powder in a suspending medium consisting essentially of an alcohol, said suspending medium acting as a solvent for a silicon alkoxide and containing a quantity of water,
(2) adding said silicon alkoxide to said suspending medium, and
(3) allowing said silicon alkoxide to hydrolyze and condense on the surface of said core particles to form said silica sol-gel;
and
(c) coating said first coating of silica gel with a second coating consisting essentially of a bismuth oxide gel by
(1) suspending said silica-gel coated particles in an alcohol, said alcohol acting as a solvent for a bismuth alkoxide and containing a quantity of water,
(2) adding said bismuth alkoxide to said suspending medium, and
(3) allowing said bismuth alkoxide to hydrolyze and condense on the surface of said first coating of silica gel to form said second coating of said bismuth oxide gel.

7 more elements

Dependencies are inferred from the claim text.