Abstract
This invention encompasses methods and reagents for making PT, PZT, and PLZT as well as their extrinsic ions doped powders and thin films. In particular, the invention includes methods for localized laser annealing of PT, PZT, PLZT films to the surface of materials to provide articles useful in electronic devices such as high value capacitors, optical switches, wave guides, and the like. A 15-25% by weight of PT/PZT/PLZT in about a 5-10% acetic acid solution having an effective wetting agent of a surfactant has been found to be a superior isolation for making both powders and thin films, especially thin films for laser writing.
Claims5
A method for forming a design of a thin ferroelectric film on a solid surface comprising:
- (a) providing a solution of about 15 to 25 percent by weight of lead titanate, lead zirconate titanate or lead lanthanum zirconate titanate in about 5-10% aqueous acetic acid solution having an effective wetting amount of a surfactant, wherein the titanium component of the solution is in the form of titanium acetate;
- (b) spin-coating the solid surface with the solution of (a);
- (c) drying the coating;
- (d) annealing a portion of the lead titanate, lead zirconate titanate or lead lanthanum zirconate titanate to the solid surface by irradiating the dried spin-coated solid surface with a laser in the desired pattern;
- and
- (e) washing the solid surface with a strong acid to remove lead titanate, lead zirconate titanate or lead lanthanum zirconate titanate not annealed by irradiation with the laser thereby leaving a pattern of the laser annealed lead titanate, lead zirconate titanate or lead lanthanum zirconate titanate on the solid surface.