Abstract

This invention relates to a process for preparing copolyester fibers having reduced spinning defects. More particularly, the invention relates to fibers having improved quality prepared from blends of certain poly(ethylene terephthalate) compositions modified with 1,4-cyclohexanedimethanol by melt spinning to produce filaments with decreased spinning defects while maintaining the chemical resistance, abrasion resistance, electrical and mechanical properties normally associated with copolyesters. These polymer blends when heated provide a fiber-forming polymer melt/dope which has excellent flowability and produces high quality fiber when subjected to conventional melt spinning, drawing, texturing, etc. Staple fibers prepared from the polymer blends of the invention when made into high loft battings have excellent fiberfill performance properties, particularly resilience and compression recovery.

Claims3

Dependent claims

A process for preparing copolyester fibers having reduced spinning defects comprising the steps of:

(I) blending
(A) 85-99 weight percent of a copolyester, Copolyester (A), having an inherent viscosity of 0.4 to 1.5 dl/g which consists essentially of
(1) a dicarboxylic acid component consisting essentially of repeat units from terephthalic acid, and
(2) a diol component consisting essentially of repeat units from 88 to 99.9 mole percent ethylene glycol and 0.1 to 12 mole percent 1,4-cyclohexanedimethanol, based on 100 mole percent dicarboxylic acid and 100 mole percent diol, and
(B) 1 to 15 weight percent of a copolyester, Copolyester (B), having an inherent viscosity of 0.4 to 1.5 dl/g which consists essentially of
(1) a dicarboxylic acid component consisting essentially of repeat units from terephthalic acid, and
(2) a diol component consisting essentially of repeat units from 40 to 82 mole percent ethylene glycol and 18 to 60 mole 1,4-cyclohexanedimethanol, based on 100 mole percent dicarboxylic and 100 mole percent diol;
the combined weights of Copolyesters (A) and (B) total 100 percent;
(II) melt spinning said blend of Copolyester (A) and (B) at temperatures of 275.degree. C. to 325.degree. C. into fiber.

6 more elements

Dependencies are inferred from the claim text.

Fibers from copolyester blends