Abrasion resistant highly filled polyester compositions

A method of coating a composition which comprises:

• (a) from 0-30 weight percent of a polybutylene terephthalate resin;
• (b) from 0-30 weight percent of a polyethylene terephthalate resin, with the proviso that the sum of the amounts of the polybutylene terephthalate resin and the polyethylene terephthalate resin must be at least 10 weight percent of the total composition;
• (c) from 10-30 weight percent of an aromatic polycarbonate resin;
• (d) an effective stabilizing amount of a stabilizer selected from the group consisting of phosphites, acidic phosphate salts, polyacid pyrophosphates and salts thereof, phosphate salts of Group IB or Group IIB metals and phosphorous oxo-acids;
• (e) from 0-10 weight percent of a styrene-rubber impact modifier;
• (f) from 30-79.99 weight percent of an inorganic filler selected from the group consisting of barium sulfate, strontium sulfate, zirconium oxide and zinc sulfate;
• and
• (g) from 0-30 percent of a fibrous glass reinforcing filler;
• said method comprising applying to said composition a curable transparent coating selected from the group consisting of:
• (a) a coating comprising a colloidal silica which is dispersed in a silanol, acrylic, methacrylic derived polymer system or mixture thereof;
• and
• (b) a coating comprising an aminoplast resin and thereafter curing said curable transparent coating composition under conditions which will cure said transparent coating.

A method of coating a composition of a article formed from a composition which comprises:

• (a) from 6-10 weight percent polybutylene terephthalate;
• (b) from 5-10 weight percent of a polyethylene terephthalate;
• (c) from 12-20 weight percent of an aromatic polycarbonate wherein in said molding composition, the ratio of polybutylene terephthalate to polyethylene terephthalate to aromatic polycarbonate is about 2:1:3;
• (d) from 0.01-5 weight percent of a stabilizer;
• (e) from 1-10 weight percent of a styrene-rubber impact modifier;
• and
• (f) from 59-72.99 weight percent of barium sulfate,
• said method comprising applying to said article a curable composition selected from the group consisting of:
• (A) a coating composition which is a dispersion of colloidal silica in a lower aliphatic alcohol-water solution of the partial condensate of a silanol of the formula RSi(OH).sub.3 in which R is selected from the group consisting of alkyl radicals of 1 to 3 carbon atoms, a vinyl radical, 3,3,3-trifluoropropyl radical, a gamma-methacryloxypropyl radical, at least 70 percent of the silanol being CH.sub.3 Si(OH).sub.3, said composition containing 10 to 50 weight percent solids consisting essentially of 10 to 70 weight percent colloidal silica and 30 to 90 weight percent of the partial condensate, said composition containing sufficient acid to provide a pH in the range of 3.0 to 6.0;
• (B) a silica-containg composition having an alkaline pH, comprising a water/aliphatic alcohol dispersion of ammonium hydroxide-stabilized colloidal silica and a partial condensate derived from organo-trialkoxy silanes;
• (C) an ultraviolet light curable coating which comprises 1-60 weight percent colloidal silica;
• 1-50 weight percent of the material produced by the hydrolysis of silyl acrylate and 25-90 weight percent of an acrylate monomer and 0.1-5 weight percent of a UV photoinitiator;
• or an ultraviolet light curable coating which comprises 100 parts by weight of colloidal silica;
• 5 to 500 parts of an acryloxy functional silane or glycidoxy functional silane;
• 10-500 parts by weight of a non-silyl acrylate and a catalytic amount of a light sensitive photoinitiator;
• and
• (D) a coating composition which is a reaction product of an aminoplast derived component and a polyester polyol consisting essentially of the reaction products of diacids and diols wherein said diacids comprise at least 50% by number of aliphatic acids in which the carbon atoms containing hydroxyl groups are separated by at least two intervening carbon atoms, and wherein the hydroxyl number is from about 50 to about 175;
• and thereafter curing said coating under curing conditions.

A method of coating an article formed from a composition which comprises:

• (a) polybutylene terephthalate 0-70 weight percent;
• (b) polyethylene terephthalate 0-70 weight percent;
• (c) polyether ester or polyetherimide ester 0-35 weight percent;
• with the proviso that the weight of (a)+(b) is at least equal to or greater than (c) and that the weight of (a)+(b) is at least 10% by weight of total composition;
• (d) from 30-80 weight percent of an inorganic filler selected from the group consisting of barium sulfate, strontium sulfate, zirconium oxide, zinc oxide and zinc sulfate;
• and
• (e) from 0-30 percent of a fibrous glass reinforcing filler,
• said method comprising applying to said composition a curable transparent coating selected from the group consisting of:
• (a) a coating comprising a colloidal silica which is dispersed in a silanol, acrylic, methacrylic derived polymer system, or mixture thereof;
• or
• (b) a coating comprising an aminoplast resin;
• and thereafter curing said curable transparent coating under conditions which will cure said transparent coating.

A method of coating a article formed from a composition which comprises:

• (a) polybutylene terephthalate 15-30 weight percent;
• (b) polyethylene terephthalate 5-15 weight percent;
• (c) polyether ester or polyetherimide ester 5-15 weight percent;
• (d) barium sulfate 40-75 weight percent;
• said method comprising applying to said article a coating composition selected from the group consisting of:
• (A) a coating composition which is a dispersion of colloidal silica in a lower aliphatic alcohol-water solution of the partial condensate of a silanol of the formula RSi(OH).sub.3 in which R is selected from the group consisting of alkyl radicals of 1 to 3 carbon atoms, a vinyl radical, 3,3,3-trifluoropropyl radical, a gamma-methacryloxypropyl radical, at least 70 percent of the silanol being CH.sub.3 Si(OH).sub.3, said composition containing 10 to 50 weight percent solids consisting essentially of 10 to 70 weight percent colloidal silica and 30 to 90 weight percent of the partial condensate, said composition containing sufficient acid to provide a pH in the range of 3.0 to 6.0;
• (B) a silica-containg composition having an alkaline pH, comprising a water/aliphatic alcohol dispersion of ammonium hydroxide-stabilized colloidal silica and a partial condensate derived from organo-trialkoxy silanes;
• (C) an ultraviolet light curable coating which comprises 1-60 weight percent colloidal silica;
• 1-50 weight percent of the material produced by the hydrolysis of silyl acrylate and 25-90 weight percent of an acrylate monomer and 0.1-5 weight percent of a photoinitiator;
• or an ultraviolet light curable coating which comprises 100 parts by weight of colloidal silica;
• 5 to 500 parts of an acryloxy functional silane or glycidoxy functional silane;
• 10-500 parts by weight of a non-silyl acrylate and a catalytic amount of a light sensitive photoinitiator;
• and
• (D) a coating composition which is a reaction product of an aminoplast derived component and a polyester polyol consisting essentially of the reaction products of diacids and diols wherein said diacids comprise at least 50% by number of aliphatic acids in which the carbon atoms containing hydroxyl groups are separated by at least two intervening carbon atoms, and wherein the hydroxyl number is from about 50 to about 175;
• and thereafter curing said coating under curing conditions.

An abrasion resistant coating for highly filled polyester-containing compositions with suitable adherence thereto, comprising:

• (a) from 0-70 weight percent of a polybutylene terephthalate resin;
• (b) from 0.14 70 weight percent of a polyethylene terephthalate resin, with the proviso that the sum of the amounts of the polybutylene terephthalate resin and the polyethylene terephthalate resin must be at least 10 weight percent of the total composition;
• (c) from 0-35 weight percent of an aromatic polycarbonate resin wherein the resin of (a)+(b) is equal to or greater than (c);
• (d) an effective stabilizing amount of a stabilizer selected from the group consisting of phosphites, acidic phosphate salts, polyacid pyrophosphates and salts thereof, phosphates of Group IB or Group IIB metals, and phosphorus oxo-acids;
• (e) from 0-15 weight percent of a styrene-rubber impact modifier;
• (f) from 0-35 weight percent of a polyetherester or polyetherimide ester resin;
• (g) from 30-80 weight percent of an inorganic filler selected from the group consisting of barium sulfate, strontium sulfate, zirconium oxide, zinc oxide and zinc sulfate;
• and
• (h) from 0-30 percent of a fibrous glass reinforcing filler;
• (i) a curable transparent coating selected from the group consisting of
• a coating comprising a colloidal silica which is dispersed in a silanol and/or acrylic or methacrylic derived polymer system;
• and
• a coating comprising an aminoplast resin.