High tabularity high chloride emulsions of exceptional stability
AssigneeEastman Kodak Company
InventorJoe E. Maskasky
Life of this patent
Estimating the term…
Abstract
A chemically sensitized high chloride tabular grain emulsion is disclosed. The tabular grains have {100} major faces. Chemically sensitized silver halide epitaxial deposits containing less than 75 percent of the chloride ion concentration of the tabular grains and accounting for less than 20 mole percent of total silver are located at one or more of the corners of the tabular grains. The emulsions are prepared by first forming the host tabular grains, epitaxially depositing silver halide selected to contain less than 50 percent of the chloride ion concentration of the tabular grains, adsorbing a photographically useful compound to the surfaces of the silver halide epitaxial deposits, and chemically digesting the emulsion.
Claims18
A radiation sensitive emulsion containing a silver halide grain population comprised of at least 50 mole percent chloride, based on total silver forming the grain population, in which greater than 30 percent of the grain population projected area is accounted for by tabular grains having an average aspect ratio of greater than 8 and a mean thickness of less than 0.3 .mu.m,
- wherein,
- the tabular grains have parallel major faces lying in {100} crystallographic planes and
- chemically sensitized silver halide epitaxial deposits containing less than 75 percent of the chloride ion concentration of the tabular grains and accounting for less than 20 mole percent of total silver are located at one or more of the corners of the tabular grains.
A process of preparing an emulsion for photographic use comprising
- forming an emulsion containing a silver halide grain population comprised of at least 50 mole percent chloride, based on total silver forming the grain population, in which greater than 30 percent of the grain population projected area is accounted for by tabular grains having an average aspect ratio of greater than 8 and a means thickness of less than 0.3 .mu.m,
- epitaxially depositing silver halide onto the tabular grains, and
- chemically sensitizing the emulsion,
- wherein,
- the tabular grains are formed with parallel major faces lying in {100} crystallographic planes,
- the silver halide epitaxial deposit is selected to contain less than 50 percent of the chloride ion concentration of the tabular grains and is deposited at a rate of less than 5.times.10.sup.-17 mol per corner-minute at a temperature of less than 45.degree. C. at one or more corners of the tabular grains,
- a photographically useful compound is adsorbed to the surfaces of the silver halide epitaxial deposits, and
- the emulsion is chemically digested to increase its photographic speed while the adsorbed photographically useful compound acts as a morphological stabilizer and restrains chloride ion invasion of the epitaxial deposits at the corners of the tabular grains during chemical digestion.
A process of preparing an emulsion for photographic use comprising
- forming an emulsion containing a silver halide grain population comprised of at least 90 mole percent chloride, based on total silver forming the grain population, in which greater than 50 percent of the grain population projected area is accounted for by tabular grains having a means thickness of less than 0.2 .mu.m,
- epitaxially depositing silver halide onto the tabular grains, and
- chemically sensitizing the emulsion,
- wherein,
- the tabular grains are formed with parallel major faces lying in {100} crystallographic planes and have an average aspect ratio of at least 12,
- the silver halide epitaxial deposit is selected to contain less than 30 percent of the chloride ion concentration of the tabular grains and is deposited at a rate of less than 5.times.10.sup.-17 mol per corner-minute at a temperature of less than 45.degree. C. at one or more corners of the tabular grains,
- a photographically useful spectral sensitizing dye, antifoggant or stabilizer containing a divalent sulfur or selenium atom is adsorbed to the surfaces of the silver halide epitaxial deposits, and
- the emulsion is chemically digested in the presence of at least one of a gold and middle chalcogen sensitizer to increase its photographic speed while the adsorbed photographically useful compound acts as a morphological stabilizer and restrains chloride ion invasion of the epitaxial deposits at the corners of the tabular grains during chemical digestion.
Dependencies are inferred from the claim text.