Back to results
US 5,208,070 AGranted
Method of aluminum plating an article
AssigneeROLLS-ROYCE plc
InventorsRobert W. Johnson, Ian K. Gillett, Paul S. J. Magrath, Colin R. Weaver
Life of this patent
Estimating the term…
Abstract
A crucible used in a powder pack plating process has an aperture below the upper surface of the powder pack to allow a density driven flow of the plating gas generated by the powder pack to move through the powder pack.
Claims2
A method of aluminum plating an article comprising the following steps:
- (a) providing an aluminising powder consisting of metallic aluminum, a volatile halide, and a refractory bulking agent;
- (b) providing a crucible adapted to receive the article, the crucible having a top closure member and an aperture in its base;
- (c) providing a retort adapted to receive the crucible, the retort having an inlet port and an outlet port whereby an inert gas may be flushed through the retort, the retort being otherwise sealable;
- (d) placing the article in the crucible, completely covering the article within the crucible with the aluminising powder, and closing the top of the crucible after the article and aluminising powder have been placed therein;
- (e) placing the crucible in the retort;
- (f) sealing the retort except for the inlet and outlet ports;
- (g) pumping an inert gas into the retort through the inlet port so as to displace air from the retort;
- (h) heating the retort so as to react the aluminum with the halide and thereby produce an aluminum halide gas which descends through the crucible and decomposes on contact with the article to deposit a layer of aluminum thereon, excess aluminum halide gas escaping through the aperture in the base of the crucible;
- and
- (i) maintaining a flow of inert gas through the retort so as to entrain excess aluminum halide escaping from the base of the crucible.
7 more elements
A method as claimed in claim 1, wherein the article is an article having a channel through it, the method replacing step (d) of claim 21 by:
- (a) providing first and second porous refractory members adapted to close respective ends of the channel;
- (b) closing the ends of the channel with the refractory members;
- and
- (c) placing the article with the closed channel in the crucible so that the channel is substantially vertical and completely covering the article within the crucible with the aluminising powder,
- whereby in steps (h) and (i) of claim 21 the refractory members prevent the aluminising powder from entering the channel but permit the passage of aluminum halide gas through the channel.
2 more elements
Dependencies are inferred from the claim text.